Magnesium and its alloys have been restricted in their industrial applications due to problems related to their formability. To overcome this issue, controlling the crystallographic texture is important, and the texture formation mechanism should be investigated in relation to factors including deformation conditions and solute atoms. In particular, the effects of solute atoms on the texture formation behavior should be further analyzed because they can considerably affect the deformation behavior. Thus, in this study, to clarify the effect of aluminum concentration on the texture formation behavior and microstructure, high-temperature uniaxial compression tests were conducted on three types of AZ-series magnesium alloys (AZ31, AZ61, and AZ91). Compression was conducted at 673 K and 723 K, with strain rates of 0.05 s⁻¹ and 0.005 s⁻¹, up to a true strain of −1.0. Cylindrical specimens were prepared from a rolled plate that had a (0001) basal texture and was compressed parallel to the c-axis of the grains. Consequently, work softening and fiber texture formation were observed in all the specimens. During the deformation, the development of grain boundaries, which is a typical characteristic of continuous dynamic recrystallization (CDRX), was observed, and the (0001) texture was highly developed with increasing Al content. Although each alloy was associated with the same deformation conditions and mechanisms, the AZ31 alloy exhibited a non-basal texture component. The stacking fault energy contributed to the generation of slip systems and gliding, and it was seen as the main reason for texture variation.

To enhance the formability of magnesium alloys, inhibition of basal texture development by the particle-stimulated nucleation (PSN) effect has attracted significant interest. However, its contribution to texture development is not easily observed due to the separation of texture from the conventional deformation behavior. This study aims to separate the Ca texture from the deformation behavior of AZX611 alloy and quantify it using scanning electron microscopy with electron backscatter diffraction (SEM-EBSD). Since Ca in the AZ61 magnesium alloy precipitated as Al₂Ca, the hot-rolled magnesium alloys AZ31, AZ61, and AZX611 were used. High temperature compression was conducted at 723 K, the strain rate 0.05/s and 0.005/s and the true strain up to −1.0. Dynamic recrystallization was observed in each specimen and the Ca-free alloys showed dislocation glide at high strain rates and solute drag at low strain rates. When the dislocation glide dominated, basal texture was strengthened. In contrast, solute drag caused non-basal texture development. Precipitation hardening caused AZ61 to have higher flow stress than those of the Ca-free alloys by the PSN effect; its texture was observed separately because the PSN grain growth around the precipitation and orientation was specific, similar to the one developed at the solute atom drag.

Controlling microstructure and texture development is a key approach to improving the formability of magnesium alloys. In this study, the effects of the strain rate and initial texture on the texture evolution of magnesium alloys during high-temperature processing are investigated. The plane strain compression of three types of AZ80 magnesium alloys with different initial textures was assessed at 723 K and a train rate of 0.0005 s⁻¹. Work softening was consistently observed in the stress–strain curves of all samples. However, the peak stress varied depending on the initial texture, with lower peak stress observed under conditions favoring prismatic slip. Under these conditions, the activation of non-basal slip suppressed the formation of basal texture. The texture shifted and developed parallel to the transverse direction when prismatic slip was dominant. In contrast, the activation of pyramidal slip led to the formation of a basal texture tilted by 25° from the $\left(0001\right)$ plane. The effects of recrystallization and grain boundary migration on texture development were minimal. This study contributes to understanding the texture development mechanisms in magnesium alloys and provides insights into improving their workability and ductility through texture modification.

For a wide industrial application of magnesium alloys, a method for imparting high damping properties while maintaining mechanical properties is required. Controlling the crystallographic texture seems to be useful, because dislocations are known to have a significant influence on the damping characteristics of magnesium alloys. In addition, textures are affected by the microstructure and texture variation when the deformation or annealing is applied. However, there were less reports about their effect on damping capacity. Therefore, the effect of twinning and annealing, which can affect the recrystallization, were investigated in this study. An AZ31 alloy was hot rolled at 673 K with a reduction ratio of 10% and 50%, and then annealed at 673 K and 723 K for 0.5, 1, 2, and 3 h, respectively. SEM-EBSD was used to examine the microstructure and texture. In addition, each specimen’s hardness and internal friction were contemporarily measured. As a result, hot rolling produced tensile twins and their fraction increased with internal friction when the reduction ratio increased. Due to annealing, a discontinuous type of static recrystallization occurred within the twinning grains, and was highly activated along with the increasing annealing temperature and the fraction of twinning. In the samples annealed at 723 K, the internal friction continuously increased over the annealing time, whereas in the samples annealed at 673 K, the decrease in dislocation density was delayed while the internal friction showed a relatively low value.