Global environmental concerns, as well as the rapid depletion of non-renewable fossil fuel-based resources, have prompted research into the development of sustainable, environmentally friendly, and biodegradable materials for use in a variety of high-end applications. To mitigate the environmental setbacks caused by nonbiodegradable materials, the development of biocomposites with improved mechanical performance is gradually gaining momentum. Natural fibers such as hemp, flax, and sisal have been well incorporated into biocomposite development. Nonetheless, the impact of functional moieties in their life cycle cannot be underestimated. In this review paper, a detailed discussion of the characteristics and components of biocomposites is presented. The treatment of composite materials (alkali and acetylation), as well as several manufacturing processes (hand layup, 3D printing, extrusion, etc.) and the applications of biocomposites, which are not limited to the aerospace industry, packaging, biomedicine, etc., are presented. Biocomposites with excellent durability, performance, serviceability, and reliability must be produced to expand their applications.

Many concerns are being expressed about the biodegradability, biocompatibility, and long-term viability of polymer-based substances. This prompted the quest for an alternative source of material that could be utilized for various purposes. Starch is widely used as a thickener, emulsifier, and binder in many food and non-food sectors, but research focuses on increasing its application beyond these areas. Due to its biodegradability, low cost, renewability, and abundance, starch is considered a “green path” raw material for generating porous substances such as aerogels, biofoams, and bioplastics, which have sparked an academic interest. Existing research has focused on strategies for developing biomaterials from organic polymers (e.g., cellulose), but there has been little research on its polysaccharide counterpart (starch). This review paper highlighted the structure of starch, the context of amylose and amylopectin, and the extraction and modification of starch with their processes and limitations. Moreover, this paper describes nanofillers, intelligent pH-sensitive films, biofoams, aerogels of various types, bioplastics, and their precursors, including drying and manufacturing. The perspectives reveal the great potential of starch-based biomaterials in food, pharmaceuticals, biomedicine, and non-food applications.

This study aims to enhance value addition to agricultural byproducts to produce composites by the solution casting technique. It is well known that PLA is moisture-sensitive and deforms at high temperatures, which limits its use in some applications. When blending with plant-based fibers, the weak point is the poor filler–matrix interface. For this reason, surface modification was carried out on hemp and flax fibers via acetylation and alkaline treatments. The fibers were milled to obtain two particle sizes of <75 μm and 149–210 μm and were blended with poly (lactic) acid at different loadings (0, 2.5%, 5%, 10%, 20%, and 30%) to form a composite film The films were characterized for their spectroscopy, physical, and mechanical properties. All the film specimens showed C–O/O–H groups and the π–π interaction in untreated flax fillers showed lignin phenolic rings in the films. It was noticed that the maximum degradation temperature occurred at 362.5 °C. The highest WVPs for untreated, alkali-treated, and acetylation-treated composites were 20 × 10⁻⁷ g·m/m² Pa·s (PLA/hemp30), 7.0 × 10⁻⁷ g·m/m² Pa·s (PLA/hemp30), and 22 × 10⁻⁷ g·m/m² Pa·s (PLA/hemp30), respectively. Increasing the filler content caused an increase in the color difference of the composite film compared with that of the neat PLA. Alkali-treated PLA/flax composites showed significant improvement in their tensile strength, elongation at break, and Young’s modulus at a 2.5 or 5% filler loading. An increase in the filler loadings caused a significant increase in the moisture absorbed, whereas the water contact angle decreased with an increasing filler concentration. Flax- and hemp-induced PLA-based composite films with 5 wt.% loadings showed a more stable compromise in all the examined properties and are expected to provide unique industrial applications with satisfactory performance.

MXene‐based biocomposites are emerging as multifunctional smart materials that combine the high electrical conductivity, tunable surface chemistry, layered architecture, and electrochemical activity of MXenes with the flexibility, processability, biocompatibility, and biodegradability of biopolymers. This review provides an assessment of MXene synthesis and structure, surface chemistry, fabrication strategies, structure–property relationships, and applications. Top–down and bottom–up synthesis routes are discussed alongside solution casting, filtration, electrospinning, freeze–drying, coating, layer‐by‐layer assembly, melt processing, and in situ polymerization. This review further highlights the electrical and thermal transport, surface chemistry, and optical and photothermal behavior of MXene‐based composites and their roles in energy storage, sensing and health monitoring, environmental remediation, electromagnetic interference (EMI) shielding, and smart food packaging. Across these applications, performance is governed by MXene loading, flake morphology, surface terminations, interfacial bonding, and suppression of restacking. Despite substantial progress, oxidation, batch variability, reproducibility, processing complexity, scalability, and long‐term stability remain significant barriers to deployment. Future research should establish quantitative structure–processing–property relationships, standardized testing, realistic durability assessment, and scalable manufacturing. Significant attention to MXene migration, ecotoxicity, life‐cycle impacts, and technoeconomic feasibility is also required. Addressing these factors will be essential for translating MXene‐based biocomposites from laboratory demonstrations into reliable, sustainable, and commercially viable technologies.