Silver (Ag) ornamented TiO₂ semiconducting nanoparticles were synthesized through the sol-gel process to be utilized as nanofillers with photo resin to enhance the mechanical and thermal properties of stereolithography 3D printed objects. The as-prepared Ag-TiO₂ nanoparticles (Ag-TNP) were typified and qualified by XRD, XPS, Raman, and FESEM; TEM analysis dissected the morphologies. The enhancement in the tensile and flexural strengths of SLR/Ag-TNP nanocomposites was noted as 60.8% and 71.8%, respectively, at the loading content of 1.0% w/w Ag-TNP within the SLR (stereolithography resin) matrix. Similarly, the thermal conductivity and thermal stability were observed as higher for SLR/Ag-TNP nanocomposites, equated to neat SLR. The nanoindentation investigation shows an excerpt hike in reduced modulus and hardness by the inclusion of Ag-TNP. The resulted thermal analysis discloses that the introduction of Ag-TNP can appreciably augment the glass transition temperature (T_g), and residual char yield of SLR nanocomposites remarkably. Hence, the significant incorporation of as-prepared Ag-TNP can act as effective nanofillers to enhance the thermal and mechanical properties of photo resin.

Fabrication of low-cost, durable and efficient metal oxide nanocomposites were successfully synthesized and reinforced with photo-resin via 3-dimensional printing. Here, we put forward a novel approach to enhance the mechanical and thermal behaviors of stereolithography (SLA) 3D printed architecture by adding TiO₂ nanoparticles (TNPs) in different crystalline phases (anatase and rutile), which were obtained at different annealing temperatures from 400 °C to 1000°C. The heat-treated anatase TNPs were scrutinized by X-ray diffraction(XRD), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, diffusive reflectance spectroscopy (DRS), and transmission electron microscopy (TEM) analysis. Among all the samples, at 800 °C, annealed anatase TNPs exposed a highly crystalline anatase phase, having a low energy bandgap and a comparably high tensile strength (47.43 MPa) and high elastic modulus (2.261 GPa) for the 3D printed samples, showing improvement by 103% and 32%, respectively, compared with the printed pristine stereolithography resin (SLR) sample. Moreover, enhanced storage modulus and tan δ values were achieved via the better interfacial interactions between the incorporated nanofillers and the SLR matrix. In addition to this, enhanced thermal conductivity and thermal stability of the SLR matrix were also noted. The low energy bandgap and nanoscale size of the fillers helped to achieve good dispersion and allowed the UV light to penetrate at a maximum depth through the photo resin.

This work investigates the effect of a modified nickel‐doped metal‐organic framework (Ni‐ZIF‐67) as a filler on thermal, mechanical, and water vapor permeability properties of environmentally friendly waterborne polyurethane (WPU). The facile and greener ultrasound (sonochemical) technique is developed to prepare multifunctional Ni‐ZIF‐67@WPU nanocomposites, exhibiting superior crystallinity and uniform distribution. The resultant Ni‐ZIF‐67 nanoparticles and Ni‐ZIF‐67@WPU films are characterized by various techniques, including powder XRD, FE‐SEM, FTIR, TGA, UTM, contact angle, and antibacterial properties. Ni‐ZIF‐67@WPU nanocomposites exhibited excellent three‐fold mechanical performance (tensile strength ≈22 MPa) at a very low 5 wt.% filler loading and high thermal stability compared to pristine WPU. In addition, Ni‐ZIF‐67@WPU exhibited optimum water vapor permeability performance at 5.0 wt.% filler with the potential antibacterial application. Demonstrate that the rapid and facile synthesis approach can enhance the interaction of filler and matrix, high surface area, and tuneable pore size of filler material. This new insight has a new green approach for fabricating advanced nanocomposites toward practical utilization.