Copper nanoparticles (CuNPs) have attracted attention due to their low cost and high specific surface area. In this work, a simple and inexpensive two-step synthesis method was proposed to prepare highly stable and well-dispersed spherical CuNPs in solution with a particle size of approximately 37 nm. Synthesis of CuNPs was carried on in the presence of complexing agent trisodium citrate (TSC), while for the chemical reduction step, sodium borohydride (NaBH₄) was used. Taking into account the potential of this type of nanoparticles, their synthesis and characterization represent a current and relevant topic in the field. The ability to control the size, shape and properties of CuNPs by adjusting the synthesis parameters (pH, precursor:stabilizer:reductant ratio, homogenization time, temperature) offers extraordinary flexibility in the development of these materials. The combination of characterization techniques such as SEM, EDX, UV–Vis, Raman, FT-IR and AFM provides a thorough understanding of the structure and properties of CuNPs, allowing the modulation of the properties of the obtained nanoparticles in the desired direction. Based on the studies, the copper reduction mechanism was proposed. For the theoretical verification of the size of the experimentally obtained spherical CuNPs, Mie theory was applied. A stability study of the synthesized CuNPs in optimal conditions was performed using UV–Vis analysis at specific time intervals (1, 3, 30 and 60 days), the sample being kept in the dark, inside a drawer at 25 °C. The CuNPs obtained after setting the optimal synthesis parameters (Cu(II):TSC:${\mathrm{B}\mathrm{H}}_4^{+}$ = 1:1:0.2, pH = 5, homogenization time 60 min and temperature 25 °C) were then tested to highlight their antibacterial effect on some reference bacterial strains. The obtained CuNPs demonstrated very good antimicrobial efficacy compared to traditional antimicrobials, for both Gram-negative and Gram-positive bacteria. This may reduce the development of antimicrobial resistance, an urgent medical issue. After evaluating the cytotoxic effects of CuNPs on the SKBR3 cancer cell line, a significant decrease in cell proliferation was observed at the 0.5 mg/mL concentration, with a reduction of 89% after 60 h of cultivation. Higher concentrations of CuNPs induced a more rapid cytotoxic effect, leading to an accelerated decline in cell viability.

The use of copper nanoparticles (CuNPs) seems to be an alternative therapeutic strategy for cancer therapy due to low-cost synthesis and anticancer activity. In this work, CuNPs’ effects were tested in various concentrations on two types of cells: mesenchymal stem cells (MSCs) and a breast cancer cell line, SKBR3. The concentrations (0.25 mM, 0.5 mM, 1 mM and 2 mM) were first tested on an impedance-based cytotoxicity assay and then used in further cellular metabolic assays. Next, several techniques were applied to test the chosen concentrations: assessment of apoptosis, intracellular reactive oxygen species (ROS) levels, oxidative stress-related gene expression, assessment of mitochondrial respiration and fatty acid methyl ester (FAME) profile evaluation. The higher CuNP concentrations tested on the SKBR3 cell line showed a dose-dependent decrease in the cell index. SKBR3 cells displayed increased CAT and SOD expression, revealed by strong dose-dependent fluorescence. Annexin/PI staining confirmed increased SKBR3 cell death induced by the higher doses of CuNPs. SKBR3 revealed higher baseline respiratory capacity compared to MSCs. Fatty acid methyl esters (FAMEs) are in higher abundance in MSCs compared to the SKBR3 cell line. The different metabolic response in the tested cells to the CuNPs’ presence could help establish a future personalized treatment for breast cancer patients.

The removal of phytotoxins from herbal preparations is important due to evidence linking exposure to aristolochic acid I (AAI), a toxin found in Aristolochiaceae species, with certain kidney diseases. This study evaluates the effectiveness of activated carbon (AC) in removing AAI from aqueous solutions and determines the optimal conditions for the process, which are necessary for accurate kinetic, thermodynamic, and equilibrium analyses. After establishing the best conditions for the adsorption reaction (pH > 6; solid/liquid ratio (S:L) = 0.1 g adsorbent: 25 mL AAI solution; contact time 120 min; temperature = 298 K, AAI initial concentration (Ci) = 150 mg/L), a maximum adsorption capacity of 10.67 mg/g was obtained. Quantitative analysis of AAI was performed using UV-VIS spectrophotometry. Experiments on kinetics, thermodynamics, and adsorption isotherms were carried out. The findings showed that the process adheres to pseudo-second-order kinetics and is spontaneous and endothermic and takes place at the interface between the adsorbent and adsorbate. The equilibrium data fits the Sips isotherm model with a regression coefficient close to 1. The findings indicate that AC is an effective material for the removal of AAI by adsorption from an aqueous solution.