The adsorption of As(V), Pb(II), Cd(II), and Cr(III) ions from aqueous solutions on natural and modified chabazite was studied. The functionalization of chabazite was performed via a protonation and calcination with the aim of generating Lewis acid sites to improve its anion exchange properties. The surface and physicochemical properties of both adsorbents were studied and compared. The adsorption isotherms of tested heavy metal ions were quantified and modeled to identify the best isotherm equation. Steric parameters for the adsorption of these ions were also calculated with a monolayer statistical physics model. Natural chabazite showed the maximum adsorption capacity for Pb(II), while the modified zeolite improved its As(V) properties in 79%. These results showed that the modified zeolite was able to remove both cations and anions from aqueous solution. The application of this functionalized chabazite can be extended for the removal of other anionic pollutants from water, thus opening the possibility of preparing new adsorbents with tailored properties for water treatment.

This study focuses on the stabilization of a natural hair dye derived from Lawsonia inermis L. (henna) and Indigofera suffruticosa (indigo). Although various formulations already exist, they are designed for immediate use and cannot be stored. Lawsonia, a primary component of the dye, tends to degrade after release. To ensure its stability, freeze-drying was implemented as a protective measure. Colorimetric analysis confirmed the dye’s ability to maintain an intense, uniform coloration even after multiple washing cycles. Stability tests demonstrate that freeze-drying effectively enhances the dye’s stability and capacity to retain its physical properties and color under various environmental conditions, demonstrating its potential for long-term use. The dye’s pH (5.05) aligns with the natural pH of hair, promoting cuticle sealing and improving hair health. Cytotoxicity tests confirmed the dye’s safety, showing no harmful effects. Gray hair exhibited a total color difference (ΔE) of 64.06 after the initial application, using natural gray hair as a reference. By the third application, ΔE increased to 69.86 and gradually decreased to 68.20 after 15 washing cycles, highlighting its long-term durability. Gray hair exposed to 720 h of UV radiation showed a ΔE of 17.34, whereas dyed gray hair exhibited a ΔE of 2.96 compared to non-UV-exposed samples. This indicates superior resistance to color degradation in dyed hair. Also, SEM imaging revealed the dye’s restorative effects, progressively improving hair cuticle structure with each application.

Entre los contaminantes más comunes en suelos y cuerpos de agua se encuentran los derivados de actividades agrícolas. El ácido 2,4-diclorofenoxiacético (2,4-D) es un compuesto perteneciente al grupo de los fenoxis y se utiliza ampliamente como herbicida selectivo. Debido a su naturaleza ionizable, puede migrar fácilmente hacia los cuerpos de agua, representando un riesgo ambiental. Una alternativa viable y económica para su remoción es la adsorción mediante biomateriales, que combinan propiedades fisicoquímicas de sus componentes para obtener características estructurales y funcionales mejoradas. En este estudio, se sintetizaron biomateriales basados en quitosano y cáscara de naranja mediante reticulación iónica. Los experimentos de adsorción de 2,4-D se realizaron a valores de pH de 3 y 5, a 25 °C y se obtuvo una capacidad máxima de adsorción de 8.3 mg g-1 a pH 3. Los biomateriales se caracterizaron mediante diversas técnicas para analizar sus propiedades estructurales y los posibles mecanismos de interacción.

En este trabajo se sintetizó un compósito magnético de hexaferrita de estroncio (SrFe12O19) con ferrita de cobalto (CoFe2O4), mediante la metodología del complejo polimérico (Pechini), con la finalidad de remover cromo (VI) en agua contaminada. La caracterización estructural, morfología y química se realizaron mediante difracción de rayos X (DRX) y espectroscopía electrónica de barrido (SEM); la medición de los sitios activos se realizó mediante el método de titulación de Boehm, y el punto isoeléctrico (IEP) se determinó mediante el potencial zeta. Los experimentos de adsorción se llevaron a cabo a pH 2, con concentraciones de Cr(VI) de 10 a 100 mg/L. Los resultados muestran que el tamaño de partícula del compósito es de 251 nm y la proporción de la mezcla es 1:1, mientras que la capacidad máxima de adsorción experimental de Cr(VI) fue de 19.72 mg/g, mientras que el modelo de Langmuir predice una capacidad de adsorción teórica de 69.29 mg/g. Debido a su alta capacidad de adsorción, sus excelentes propiedades magnéticas (que facilitan su recuperación) y sus bajos costos de producción, este material constituye una opción prometedora para la eliminación del cromo (VI) del agua contaminada.