This study evaluated the corrosion inhibitory effects of Ruta graveolens leaf extract for 304 stainless steel in 1 M HCl. The analysis of the leaf extract using HPLC indicated that the primary compounds present in the leaf extract were rutin, caffeic acid, p-coumaric acid, and apigenin. The inhibition efficiency (IE%) of the extract was studied using weight loss, potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and computational simulation (density functional theory, DFT). The effects of the inhibitor concentration and solution temperature were investigated. The results indicated that the IE% increased for increasing concentrations of the extract, while the reverse was true with increasing temperatures. At 25 °C and a 600 ppm extract concentration, the results indicated a maximum inhibition efficiency of 95%, 98%, and 96% by weight loss, potentiodynamic polarization, and EIS techniques, respectively. SEM observations showed a significant change in the surface morphology of the 304 SS with and without the addition of the inhibitor compound. At all temperatures, the adsorption of the inhibitor components onto the 304 SS surface was found to follow the Langmuir isotherm model, and the inhibition process was governed by physical adsorption. Furthermore, chemical interactions between the inhibitor and the 304 SS steel surface were elucidated via density functional theory (DFT) calculations.

ZnO-based ceramic varistors have shown excellent electrical and dielectric properties due to their characteristics microstructures represented by the arrangement of their grains and grain boundaries that allow the absorption and flow of energy when subjected to an electrical surge. Their properties and characteristics depend on their chemical compositions and processing routes. Typical processing routes involve several stages of grinding and precalcination—which are time consuming processes. Because of this, this study proposes a simpler and cheaper alternative route for processing ceramic varistors. The alternative process proposed is the mixing of the precursor oxides by means of a hydrothermal treatment. The characteristics and properties of the synthesized ceramic varistors were evaluated by means of scanning electron microscopy, X-ray diffraction and impedance spectroscopy, considering the effect of the addition of rare earth oxides (La₂O₃, CeO₂ and Nd₂O₃). The results showed that the mixing of the oxides through hydrothermal treatment produces ceramic varistors with characteristics and properties similar to those obtained by other processing routes. Furthermore, it was observed that the addition of rare earth oxides affects the characteristics and properties of the ceramic varistor depending on the type of rare earth oxide added, its concentration and ionic radius.

In this work, the effect of the addition of noble metals on the order–order disorder process of the L12 structure corresponding to the intermetallic Ni₃Al is analyzed. Stoichiometric, nonstoichiometric, and quasi-binary compositions doped with noble metals such as Ag, Au, Pd, and Pt (1 at%) were analyzed. It was observed that depending on the composition, there is a modification in the activation energies calculated from the two time constants that characterize the disorder process. The statistic of atomic jumps was typified based on the configuration of the window to be crossed and, with this, it was identified that the origin of the negative activation energy of the long disorder process is due to an increase in the corresponding energy of the Al_Al-Ni jump through unnatural windows.

Cr₂Nb alloys are potential candidates for high-temperature structural materials. The influence of different mechanical alloying parameters (milling time) and sintering processes were studied. After mechanical alloying and observation by scanning electron microscope (SEM), nano powders were characterized and then sintered by spark plasma sintering (SPS). Electrochemical noise (EN) tests were also conducted in order to study the electrochemical behavior. From the current experimental results, it was revealed that ball milling times up to 20 h may explain the influence of Nb–Cr alloys and its association to the Laves phase and corrosion behavior. These insights aimed at improving the samples’ predicted behavior before spending time and resources at high-temperature industrial processes.

Al–Cu–Mg composites reinforced with sub-micron tungsten carbide (WC) particles were synthesized by powder metallurgy and subjected to T6 heat treatment to clarify the interplay between dispersion strengthening and precipitation hardening. Composites with 1–3 wt.% WC (average size 0.8 μm) were solution-treated at 540 °C for 3 h, water-quenched, and aged at 195 °C for up to 100 h. Microstructural analyses confirmed a uniform distribution of WC and demonstrated that its presence did not modify the dissolution–precipitation sequence of the Al-Cu-Mg matrix. Transmission Electron Microscopy observations provided direct evidence of θ′ (Al₂Cu) precipitates. The 3 wt.% WC composite reached peak hardness after 5 h (78 HRF), a 15% increase over the T6-treated unreinforced alloy, and exhibited a 40% higher yield strength (330 MPa). These improvements were attributed to the combined effects of Orowan strengthening and age-hardening precipitates (θ′). The results demonstrate that integrating powder metallurgy, sub-micron WC reinforcement, and T6 treatment is an effective route to enhance strength in Al–Cu–Mg alloys without delaying aging kinetics.

In this work, titanium dioxide scaffolds were synthesized. Titanium isopropoxide (IV) was used as a precursor in its formation, using a polymeric network of galactopyranose as a template. The powder sample obtained was evaluated by scanning tunneling microscopy (STM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) analysis, and thermal gravimetric analysis (TGA-DTA). According to the results, it was found that these scaffolds can be successfully synthesized in solution using the sol-gel method. The synthesized scaffolds have diameters from 50 nm with porosity of approximately 0.3–10 nm. Important parameters, such as pH and the concentration of the metallic precursors, were optimized in this solution. The values of maximum average roughness R(max) and roughness value (Ra) were 0.50 and 1.45, respectively. XRD diffraction analysis shows the formation of crystalline phases in the TiO₂ scaffold at 700 °C. The use of biological polymers represents an alternative for the synthesis of new materials at low cost, manipulating the conditions in the production processes and making the proposed system more efficient.