This paper describes the processing conditions needed to produce low density nanocellular polymers based on polymethylmethacrylate (PMMA) with relative densities between 0.45 and 0.25, cell sizes between 200 and 250 nm and cell densities higher than 10¹⁴ cells/cm³. To produce these nanocellular polymers, the foaming parameters of the gas dissolution foaming technique using CO₂ as blowing agent have been optimized. Taking into account previous works, the amount of CO₂ uptake was maintained constant (31% by weight) for all the materials. Foaming parameters were modified between 40 °C and 110 °C for the foaming temperature and from 1 to 5 min for the foaming time. Foaming temperatures in the range of 80 to 100 °C and foaming times of 2 min allow for production of nanocellular polymers with relative densities as low as 0.25. Cellular structure has been studied in-depth to obtain the processing-cellular structure relationship. In addition, it has been proved that the glass transition temperature depends on the cellular structure. This effect is associated with a confinement of the polymer in the cell walls, and is one of the key reasons for the improved properties of nanocellular polymers.

The evolution of technology means that increasingly better materials are needed. It is well known that as a result of their interesting properties, nanocellular polymers perform better than microcellular ones. For this reason, the investigation on nanocellular materials is nowadays a very topical issue. In this paper, the different approaches for the production of these materials in our laboratory are explained, and results obtained by using polymethylmethacrylate (PMMA) are shown. Homogeneous nucleation has been studied by using raw PMMA, while two different systems were used for heterogeneous nucleation; adding nanoparticles to the system and using nanostructured polymers as solid precursors for foaming. The effects of the different parameters of the production process (gas dissolution foaming process) have been evaluated for all systems being possible to establish a comparison between the materials produced by different approaches. Moreover, the limitations and future work to optimise the materials produced are also discussed.