Additive manufacturing processes have been developed over the last decades, especially vat photopolymerization (VP) processes, due to its simplicity and speed. The objective of this paper is to characterize commercial VP resins widely used for technical applications. Thus, test specimens were printed by Digital Light Processing and subjected to tensile, compression, flexural, hardness, and inorganic composition analyses. The resin with the highest resistance and hardness (containing 0.6 vol% of inorganics load) reached 53 MPa in tension, 110 MPa in compression, 79 MPa in bending, and 82.3 Shore D, which is comparable to injected polymers. A case study was made, replacing the injected gears of a reducer by printed ones and comparing the finite element analysis with resin properties. The characterization and case study results encourage the expansion of VP processes in the manufacturing of products in several industries and service sectors, as well as the development of new composite resins.

Niobium-based oxides have garnered increased attention in recent years for their remarkable enhancement of corrosion resistance, as well as biofunctional properties of various metallic materials, including 316L SS. However, the mechanical properties of these promising coatings have not been fully elucidated. This study investigated how much the environmental conditions (air, artificial saliva, and NaCl solution) impact the wear performance of 316L SS without and with Nb₂O₅ coatings deposited via the reactive sputtering technique. The results exhibited a notable decrease in friction coefficient (55% in air, 18% in artificial saliva, 10% in 0.9 wt% NaCl solution), wear area (46% in air, 36% in AS, 17.5% in 0.9 wt% NaCl solution), and wear rate (44.0% in air, 19.5% in AS, 12.0% in 0.9 wt% NaCl solution). Ultimately, the results obtained in the present study elucidate the synergistic mechanisms of corrosion and wear in 316L SS containing Nb₂O₅ coatings, highlighting its significant potential for applications in the biomedical sector.