Hexagonal single crystal nanosheets of Nd³⁺ doped PbI₂ were effortlessly synthesized via microwave-assisted technique under a power of 700 W and in a duration of 15 minutes with a homogeneous morphology. X-ray diffraction, energy dispersive X-ray spectroscope, scanning electron microscope, FT-Raman, UV-Visible, photoluminescence and dielectric measurement were employed to study the product. High purity, single phase and presence of Nd³⁺ doping was confirmed. SEM study confirm the formation of nanorods and single crystal nanosheets of very few nanometers in size. Robust vibrational analysis has been carried out and the observed bands are assigned to the vibration modes of E₂¹, A₁¹, A₁², 2E₂¹ and 2E₁¹, respectively. These bands are red-shifted when compare to the corresponding bulk values which indicate relaxed nanostructure formation and occurrence of confinement effect. The thickness of the synthesized single crystal nanosheets are found to be in the range of ~20 to 30 nm. The energy band gap was calculated and found to be 3.35, 3.34, 3.42 and 3.39 eV for pure, 1, 3 and 5% Nd³⁺ doped lead iodide, respectively. The clear blue luminescence has been observed at 440 nm and 466 nm when excited at 250 nm and 280 nm respectively. Dielectric and ac electrical conductivity was also measured and discussed.

The current study is focused on the donor–bridge–acceptor (D–π–A) type of novel organic charge transport and non-linear optical material, 1-(4-bromophenyl)-3-(2,4,5-trimethoxyphenyl) prop-2-en-1-one (2,4,5-TMBC) to spotlight its various important properties through experimental and quantum chemical approaches. The compound 2,4,5-TMBC was synthesized via a Claisen–Schmidt condensation reaction and its single crystal was grown by a slow evaporation solution growth technique. FT-IR and FT-Raman spectra of 2,4,5-TMBC were obtained and investigated. The molecular geometry of 2,4,5-TMBC was optimized by HF, B3LYP, CAM-B3LYP, wb97xd and LC-BLYP methods using the 6-31G* basis set. The calculated geometrical parameters and vibrational spectra are in good agreement with the experimental results. Time dependent density functional theory (TD-DFT) has been applied to investigate the optical properties of the title compound. The absorption wavelength calculated at the TD-B3LYP/6-31G* level of theory in the gas phase was in good agreement with the experimental value (∼400 nm) when compared with other methods. The HOMO–LUMO energy gap was calculated at all the applied levels of theory. The total dipole moment, polarizability, anisotropy of polarizability and static first and total hyperpolarizability values of 2,4,5-TMBC were calculated at different levels of theory. The dipole moment and first hyperpolarizability values are found to be many folds (2 and 56 times calculated at B3LYP) higher than urea. It is also expected that 2,4,5-TMBC would be electron transport material due to its smaller electron reorganization energy value. The study of non-linear optical (NLO) properties shows that 2,4,5-TMBC would be an outstanding candidate for NLO device applications.