The paper details a comprehensive experimental investigation on the influence of operating parameters and cut direction (parallel and perpendicular to fibre orientation) when wire electrical discharge machining (WEDM) unidirectional CFRP composites using zinc-coated brass wire (0.25-mm diameter). A Taguchi L18 fractional factorial orthogonal array considering four variable parameters including open voltage, ignition current and pulse-on time as well as pulse-off time was carried out for each cut direction. Results showed that a ~ 16% increase in maximum material removal rate was achieved when machining parallel to fibre direction (2.41 mm³/min) compared to cutting perpendicular to the fibres (~ 2.08 mm³/min), which was attributed to the higher electrical conductivity of the workpiece along the fibre length leading to greater discharge energies. This however resulted in relatively larger average kerf widths and poorer workpiece surface roughness (Sa) caused by the Joule heating effect. Workpieces machined parallel to fibre direction were generally free of any major edge defects, in contrast to severe delamination observed on both the top and bottom surfaces of specimens cut perpendicular to fibre orientation. High-magnification scanning electron microscopy of the machined surfaces revealed the presence of adhered resin material, fibre cracking, cavities/gaps in the matrix phase and interlayer cracks on most of the samples analysed, with damage severity dependent on the operating parameters and cut direction.

This paper presents a study conducted to examine the effect of cutting parameters, namely standoff distance, nozzle traverse speed (TS), abrasive flow rate (AFR), and material type on cutting performance for two types of marble workpieces, Carrara white and Indian green. Statistical analysis was undertaken to assess the influence of the cutting parameters on the process performances in terms of surface roughness, surface waviness, and Kerf taper ratio. The results showed that the TS and material type were the most significant factors that affected surface roughness and Kerf taper ratio. Also, although AFR was found to have significant effect on surface waviness, it had no noticeable influence on surface roughness nor Kerf taper ratio.

Due to the abrasive nature of the material, the conventional machining of CFRP composites is typically characterised by high mechanical forces and poor tool life, which can have a detrimental effect on workpiece surface quality, mechanical properties, dimensional accuracy, and, ultimately, functional performance. The present paper details an experimental investigation to assess the feasibility of wire electrical discharge machining (WEDM) as an alternative for cutting multidirectional CFRP composite laminates using high-performance wire electrodes. A full factorial experimental array comprising a total of 8 tests was employed to evaluate the effect of varying ignition current (3 and 5 A), pulse-off time (8 and 10 µs), and wire type (Topas Plus D and Compeed) on material removal rate (MRR), kerf width, workpiece surface roughness, and surface damage. The Compeed wire achieved a lower MRR of up to ~40% compared with the Topas wire when operating at comparable cutting parameters, despite having a higher electrical conductivity. Statistical investigation involving analysis of variance (ANOVA) showed that the pulse-off time was the only significant factor impacting the material removal rate, with a percentage contribution ratio of 67.76%. In terms of cut accuracy and surface quality, machining with the Compeed wire resulted in marginally wider kerfs (~8%) and a higher workpiece surface roughness (~11%) compared to the Topas wire, with maximum recorded values of 374.38 µm and 27.53 µm Sa, respectively. Micrographs from scanning electron microscopy revealed the presence of considerable fibre fragments, voids, and adhered re-solidified matrix material on the machined surfaces, which was likely due to the thermal nature of the WEDM process. The research demonstrated the viability of WEDM for cutting relatively thick (9 mm) multidirectional CFRP laminates without the need for employing conductive assistive electrodes. The advanced coated wire electrodes used in combination with higher ignition current and lower pulse-off time levels resulted in an increased MRR of up to ~15 mm³/min.

Electro-discharge machining (EDM) has been extensively employed for machining hard alloys, and its simulations have been widely conducted using finite element analysis (FEA). However, the majority of mesh-based models depended on forecasting the crater profile only based on the temperature gradient, without offering detailed data regarding the machined material properties. It is crucial to understand the behaviour of the machined material in order to accurately assess the flushing efficiency, analyse the wear on the electrode, and examine the interaction between the debris generated during machining and the remaining workpiece. This is done to ensure that no recast material is left behind after the EDM process. For the first time, a meshless smoothed particle hydrodynamics multi-phase model was implemented to gain practical insights and comprehensively understand a very intricate phenomenon that occurs within a very short time. Additionally, this approach is utilised to investigate the characteristics of the materials being machined. We utilised our SPH model to simulate both the capacitance- and transistor-based EDM of Ti–6Al–4V and AISI304 steel. Our simulation considered the temperature-dependent thermal properties and latent heats of the materials. The accuracy of our model was confirmed by comparing its results with experimental, analytical, and finite element analysis (FEA) results. The machined material was observed during its removal from the surface, and the dimensions of the resulting crater, as well as its aspect ratio and the rate at which the material was removed, were predicted with an error ranging from 2 to 22%. This error is far lower than that of the typical finite element (FE) prediction. This model lays the groundwork for a more complex model that will more accurately represent EDM and other similar manufacturing processes.

Conventional drilling of carbon fibre–reinforced plastic (CFRP) presents significant challenges due to the material’s abrasive nature and anisotropic properties, leading to tool wear, delamination, and surface damage. To address these challenges, this study pioneers the use of wire electrical discharge machining (WEDM) to evaluate the drilling performance of thick CFRP lay-up configurations mainly unidirectional and multidirectional, marking the first application of WEDM for CFRP drilling. The study evaluates material removal rate (MRR), delamination factor (DF), and surface damage while employing an analytical solution to estimate surface temperature and heat conduction in the laminates. An eight-full factorial experimental design was employed, involving variations in ignition current (3 A and 5 A) and pulse-off time (4 µs and 8 µs). The findings revealed that the multidirectional lay-up achieved an MRR of 2.85 mm³/min, significantly outperforming the unidirectional lay-up’s MRR of 0.95 mm³/min, representing a 300% increase at 5 A and 4 µs. However, the increase in discharge energy led to surface damage such as delamination, frayed fibres, and irregular circularity, especially evident in the unidirectional lay-up. For delamination, the multidirectional lay-up had the highest top DF of 1.4 at 5 A and 6 µs, while the unidirectional lay-up achieved the peak bottom DF of 1.24 at the same levels. While none of the parameters significantly affected the responses, the current exhibited the highest contribution ratios. Analytical predictions of the thermal distribution indicated a 45-µm delamination length at the laminate surface and depth, aligning closely with experimental predictions of 30–50 µm.