The hydrogen economy is the key solution to secure a long-term energy future. Hydrogen production, storage, transportation, and its usage completes the unit of an economic system. These areas have been the topics of discussion for the past few decades. However, its storage methods have conflicted for on-board hydrogen applications. In this review, the promising systems based on solid-state hydrogen storage are discussed. It works generally on the principles of chemisorption and physisorption. The usage of hydrogen packing material in the system enhances volumetric and gravimetric densities of the system and helps in improving ambient conditions and system kinetics. Numerous aspects like pore size, surface area ligand functionalization and pore volume of the materials are intensively discussed. This review also examines the newly developed research based on MOF (Metal-Organic Frameworks). These hybrid clusters are employed for nano-confinement of hydrogen at elevated temperatures. A combination of the various methodologies may give another course to a wide scope in the area of energy storage materials later in the future.

Carbon materials and their allotropes have been involved significantly in our daily lives. Zero‐dimensional (0D) fullerenes, one‐dimensional (1D) carbon materials, and two‐dimensional (2D) graphene materials have distinctive properties and thus received immense attention from the early 2000s. To meet the growing demand for these materials in applications like energy storage, electrochemical catalysis, and environmental remediation, the special category, i.e., three‐dimensional (3D) structures assembled from graphene sheets, has been developed. Graphene oxide is a chemically altered graphene, the desired building block for 3D graphene matter (i.e., 3D graphene macrostructures). A simple synthesis route and pore morphologies make 3D reduced‐graphene oxide (rGO) a major candidate for the 3D graphene group. To obtain target‐specific 3D rGO, its synthesis mechanism plays an important role. Hence, in this article, we will discuss the general mechanism for 3D rGO synthesis, vital procedures for fabricating advanced 3D rGO, and important aspects controlling the growth of 3D rGO.

The objective of this paper was to determine the optimum process parameters of an electric discharge machine while machining a new hybrid aluminum metal matrix composite. In this study, a new hybrid aluminum metal matrix composite was prepared, with silicon carbide and graphite particles used as reinforcements, with the help of the stir casting method. The selected electric discharge machining parameters in this study were peak current (I), voltage (V), pulse-on time (T_on), and tool material, while the response parameters were material removal rate and surface roughness. To machine the fabricated samples, two different types of tool materials (copper and brass) were used as electric discharge machine electrodes, and each had a diameter (Ø) of 12.0 mm. The optimal settings of the electric discharge machining parameters were determined through experiments planned, conducted, and analyzed using the Taguchi (L₁₈) technique. An analysis of variance and confirmatory tests were used to check the contribution of each machining parameter. It was found that the material removal rate increased with the increase in pulse-on time and pulse current, whereas the material removal rate decreased with the increase in voltage. On the other hand, reduced surface roughness could only be achieved when current, voltage, and pulse duration were low. It was also found that the selected electric discharge machining electrodes had a significant effect on both the material removal rate and the surface roughness.