Polyurethane (PUR) soft foams release malodorous and potentially toxic compounds when exposed to oxidative conditions. Current chamber test methods cannot distinguish between pre-existing volatiles and those formed during oxidation, nor can they assess the formation rates of oxidation products. We subjected PUR soft foam to oxidative treatment in a continuous air flow at 120 °C. Emissions were convectively transferred from the foam to an exhaust port and analyzed using a thermodesorption–gas chromatography–mass spectrometry (TD-GC-MS) system, with external calibration employed for the quantification of selected analytes. The study identified hydroperoxide formation and degradation as key mechanisms in the breakdown of the polyether soft segments. This process predominantly produces volatiles, such as carboxylic acids, formates, acetates, alpha-hydroxy-ketones, (unsaturated) aldehydes, substituted dioxolanes and dioxanes, glycols, and allyl ethers. Volatiles associated with the degradation of the hard segments include aniline, benzoxazole, 2-methylbenzoxazole, and benzaldehyde. This experimental setup enables reproducible qualitative and quantitative analysis of volatiles formed during the oxidative degradation of PUR soft foams, providing new insights into the segment-dependent chemical pathways of the polymer’s molecular breakdown.

A series of new flame retardants (FR) based on dibenzo[d,f][1,3,2]dioxaphosphepine 6-oxide (BPPO) incorporating acrylates and benzoquinone were developed previously. In this study, we examine the fire behavior of the new flame retardants in polyisocyanurate (PIR) foams. The foam characteristics, thermal decomposition, and fire behavior are investigated. The fire properties of the foams containing BPPO-based derivatives were found to depend on the chemical structure of the substituents. We also compare our results to state-of-the-art non-halogenated FR such as triphenylphosphate and chemically similar phosphinate, i.e. 9,10-dihydro-9-oxa-10- phosphaphenanthrene-10-oxide (DOPO), based derivatives to discuss the role of the phosphorus oxidation state.

The impact of phosphorus-containing flame retardants (FR) on rigid polyisocyanurate (PIR) foams is studied by systematic variation of the chemical structure of the FR, including non-NCO-reactive and NCO-reactive dibenzo[d,f][1,3,2]dioxaphosphepine 6-oxide (BPPO)- and 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO)-containing compounds, among them a number of compounds not reported so far. These PIR foams are compared with PIR foams without FR and with standard FRs with respect to foam properties, thermal decomposition, and fire behavior. Although BPPO and DOPO differ by just one oxygen atom, the impact on the FR properties is very significant: when the FR is a filler or a dangling (dead) end in the PIR polymer network, DOPO is more effective than BPPO. When the FR is a subunit of a diol and it is fully incorporated in the PIR network, BPPO delivers superior results.

The oxidation of flexible polyurethane (PUR) foams significantly impacts product durability, vehicle indoor air quality, and volatile organic compound (VOC) emissions. This study investigates oxidation kinetics and VOC emissions (65–155 °C) from foams with indices between 70 and 115 (molar ratio of NCO to NCO-reactive groups × 100), where a higher index represents greater hard segment (methylene diphenyl diisocyanate) and lower soft segment (polyether polyol) content. Using a flow-through setup with PTFE chambers and Tenax thermodesorption tubes and dinitrophenylhydrazine (DNPH) cartridges, VOCs from initial analyte loading, hydroperoxide degradation, and autoxidation were distinguished, providing robust kinetic data unaffected by diffusion interference. A higher index accelerated soft segment degradation, increasing oxidation rates and VOC emissions. The activation energy of 1,2-propanediol-1-acetate-2-formate increased from 87 kJ/mol in low-index to 108 kJ/mol in high-index formulations. VOC emissions from high-index foams were tripled for acetaldehyde during long-term aging at 65 °C. While most emissions followed Arrhenius behavior, formaldehyde and acrolein deviated above 100 °C, with higher hard-segment content extending their Arrhenius range. These findings link PUR composition to degradation behavior and emissions, enabling formulation improvements. The results advance methods for evaluating raw material contributions and the performance of antioxidants under realistic aging conditions.