Bismuth based quaternary glasses with compositions BiBLM: 50Bi₂O₃–20B₂O₃–15Li₂O–15MO (where MO = ZnO, CdO, BaO, and PbO) were processed by conventional melt quenching. The effectiveness of various modifier oxides on the optical and structural properties of the developed glasses was studied systematically by XRD, DSC, FTIR, Raman, and optical absorption (OA) measurements. The synthesized glass specimens were characterized by XRD and the patterns demonstrated an amorphous nature. The physical characteristics such as molar mass, density, and OPD values were found to increase with an increase in the molar mass of the modifier oxides, while there was a decrement in oxygen molar volume, thus resulting in decrement of complete molar volume of the prepared glasses. From DSC analysis, incorrigible reduction and enhancement of T_g and thermal stability among various modifier oxides in the glass network was noticed. Optical absorption data for glass specimens have confirmed the decrease in both direct and indirect optical band gap values among various modifier oxides incorporation. These investigations support the obtained Urbach energy (UE) and metallization criteria of synthesized glasses. The ionic characteristic for the glass specimens were confirmed by the values of electronic polarizability and electronegativity. The Raman and FT-IR spectra of the glass specimens displayed the existence of BiO₃, BiO₆, ZnO₄, CdO₄, BaO₄, BO₃, PbO₄, and BO₄ structural units within the glass matrix. These structural results can support the applications of as-developed glasses in the area of photonics.

This paper deals with the investigation of a variety of physical properties including dielectric constant (over a wide range of frequency and temperature), optical absorption, luminescence, electron spin resonance (ESR) and infrared spectra of a TiO₂-doped lead molybdenum borate glass system. The composition chosen for the study is 30PbO–4MoO₃–(66–x)B₂O₃:xTiO₂ (with x ranging from 0.2 to 2.0). Quantitative analysis of the results of this study shows that, when the content of TiO₂ is around 0.8 mol%, the titanium ions exist predominantly in the tetravalent state and occupy substitutional positions in the glass network. A substantial increase in the insulating strength of these glasses on TiO₂ doping has also been observed. When the concentration of TiO₂ is increased beyond 0.8 mol%, it is observed that titanium ions exist primarily in the Ti³⁺ state and molybdenum ions in the Mo⁵⁺ state; analysis of the results further suggests that both of these ions participate in the depolymerization of the glass network.