Green synthesis is an easy, safe, and environmentally beneficial nanoparticle creation method. It is a great challenge to simultaneously improve the capping and stabilizing agent carrier separation efficiency of photocatalysts. Herein, Zn-doped Titanium dioxide (TiO₂) nanoparticles with high exposure of 360 nm using a UV/visible spectrophotometer were prepared via a one-step hydrothermal decomposition method. A detailed analysis reveals that the electronic structures were modulated by Zn doping; thus, the responsive wavelength was extended to 600 nm, which effectively improved the visible light absorption of TiO₂. We have optimized the different parameters like concentration, time, and temperature. The peak for TiO₂ is located at 600 cm-¹ in FTIR. A scanning electron microscope revealed that TiO₂ has a definite shape and morphology. The synthesized Zn-doped TiO₂NPs were applied against various pathogens to study their anti-bacterial potentials. The anti-bacterial activity of Zn-doped TiO₂ has shown robust against two gram-ve bacteria (Salmonella and Escherichia coli) and two gram + ve bacteria (Staphylococcus epidermidis and Staphylococcus aureus). Synthesized Zn-doped TiO₂ has demonstrated strong antifungal efficacy against a variety of fungi. Moreover, doping TiO₂ nanoparticles with metal oxide greatly improves their characteristics; as a result, doped metal oxide nanoparticles perform better than doped and un-doped metal oxide nanoparticles. Compared to pure TiO₂, Zn-doped TiO₂ nanoparticles exhibit considerable applications including antimicrobial treatment and water purification.

With the progression of nanotechnology, the use of nanoparticles (NPs) in consumer products has increased dramatically and green synthesis is one of the cheapest and eco‐friendly methods to obtain non‐hazardous NPs. In the current research zinc (Zn) NPs synthesis was carried out by using the fresh and healthy leaves of Mentha arvensis L. followed by characterisation through ultraviolet (UV)–visible spectroscopy, X‐ray diffraction (XRD) and scanning electron microscopy (SEM). UV–visible spectroscopy confirmed the green synthesis of ZnNPs, while XRD confirmed the size of NPs, which was 30–70 nm. SEM shows that the shape of ZnNPs was irregular. The effects of green synthesised NPs on two different varieties of Brassica napus were evaluated. Exposure to ZnNPs (5, 15, and 25 mg/l ⁻¹ ) caused a significant increase in root and shoot length of B. napus. The application of NPs significantly improved plant germination and triggered the production of secondary metabolite and antioxidant enzymes. ZnNPs showed a significant increase in chlorophyll, superoxide dismutase, total flavonoid content (TFC) and antioxidant enzymes while total phenolic content was decreased when TFC increased. Thus, it has been concluded from the current study that ZnNPs may possibly trigger the production of antioxidant enzymes and various biochemical compounds.

Microwave synthesized (low energy) ZV-FeNPs stabilised with Mentha piperita extract removed >80% of phosphate, ammonia, nitrate, lead and chloride, typical agricultural run-off contaminants, from UK canal water with a single application for 24 h.

Herein, a unique synthetic approach called microemulsion is used to create nickel nanoparticles (Ni-NPs). SEM, TEM, EDX, and XRD techniques were employed for the investigation of morphology and structures of the synthesized material. Electrons from electroactive components are transferred to external circuits by Ni-NPs’ superior electrical conductivity and interconnected nanostructures, which also provide a large number of channels for ion diffusion and additional active sites. The experimental findings showed that as a positive electrode for supercapacitors (SC), Ni-NPs had an outstanding ability to store charge, with a dominant capacitive charge storage of 72.4% when measured at 10 mV/s. Furthermore, at 1 A/g, Ni-NP electrodes exhibit a maximum capacitance of 730 F/g. Further, the Ni-NP electrode retains 92.4% of its capacitance even for 5000 cycles, highlighting possible applications for it in the developing field of renewable energy. The current study provides a new method for producing high-rate next-generation electrodes for supercapacitors.