We propose a simple method for the efficient and rapid synthesis of one-dimensional hematite (α-Fe₂O₃) nanostructures based on electrical resistive heating of iron wire under ambient conditions. Typically, 1–5 μm long α-Fe₂O₃ nanowires were synthesized on a time scale of seconds at temperatures of around 700 ° ⊂. The morphology, structure, and mechanism of formation of the nanowires were studied by scanning and transmission electron microscopies, energy dispersive X-ray spectroscopy, X-ray photoelectron spectroscopy, and Raman techniques. A nanowire growth mechanism based on diffusion of iron ions to the surface through grain boundaries and to the growing wire tip through stacking fault defects and due to surface diffusion is proposed.

Nanowires (NWs) of metal oxides (Fe(2)O(3), CuO, V(2)O(5) and ZnO) were grown by an efficient non-catalytic economically favorable method based on resistive heating of pure metal wires or foils at ambient conditions. The growth rate of iron oxide NWs exceeds 100 nm s(-1). Produced NWs were typically 1-5 microm long with diameters from 10 to 50 nm. The produced metal oxide NWs were characterized by means of SEM, TEM, EDX, XPS and Raman techniques. The field emission measurements from the as-produced CuO NWs were found to have a threshold field as low as 4 V microm(-1) at 0.01 mA cm(-2). The formation mechanism of the NWs is discussed.

Superhydrophobic surfaces are important parts of many applications in cleaning and protective coatings. Such surfaces can be realized by controlling the surface chemistry and nanoscale structure. Elongated ZnO nanostructures, called nanowires, are often used in superhydrophobic applications due to their intrinsic characteristic advantages and simple synthesis control. This review presents a critical overview of the latest research activities focused on the ZnO nanowire superhydrophobic surfaces. A wettability mechanism background is introduced with the overlay of the crystal structure fundamentals adapted for ZnO nanowires to gain insights into the multifunction application of superhydrophobic ZnO nanowires. Moreover, the latest achievements in application of ZnO superhydrophobic nanowires or reversible wettability for self-cleaning, separation, antifogging, antibacterial, and other applications are outlined. Finally, a brief outlook on the issues and emerging perspectives of ZnO nanowire wettability research is summarized.

This article provides an overview of the recent development of ZnO nanowires (NWs) for chemoresistive sensing. Working mechanisms of chemoresistive sensors are unified for gas, ultraviolet (UV) and bio sensor types: single nanowire and nanowire junction sensors are described, giving the overview for a simple sensor manufacture by multiple nanowire junctions. ZnO NW surface functionalization is discussed, and how this effects the sensing is explained. Further, novel approaches for sensing, using ZnO NW functionalization with other materials such as metal nanoparticles or heterojunctions, are explained, and limiting factors and possible improvements are discussed. The review concludes with the insights and recommendations for the future improvement of the ZnO NW chemoresistive sensing.