The functional silica/polyamide-imide composite films were prepared via simple ultrasonic blending, after the silica nanoparticles were modified by cationic surfactant—cetyltrimethyl ammonium bromide (CTAB). The composite films were characterized by scanning electron microscope (SEM), thermo gravimetric analysis (TGA) and thermomechanical analysis (TMA). CTAB-modified silica nanoparticles were well dispersed in the polyamide-imide matrix, and the amount of silica nanoparticles to PAI was investigated to be from 2 to 10 wt%. Especially, the coefficients of thermal expansion (CET) continuously decreased with the amount of silica particles increasing. The high thermal stability and low coefficient of thermal expansion showed that the nanocomposite films can be widely used in the enamel wire industry.

Background: Rhodamine B (RhB) is widely used as a colorant in textiles and food stuffs, and is also a well-known water tracer fluorescent. It is harmful to human beings and animals, and causes irritation of the skin, eyes and respiratory tract. The carcinogenicity, reproductive and developmental toxicity, neurotoxicity and chronic toxicity toward humans and animals have been experimentally proven. RhB cannot be effectively removed by biological treatment due to the slow kinetics. Therefore, RhB is chosen as a model pollutant for liquid phase plasma (LPP) treatment in the present investigation. Results: This paper presents experimental results for the bleaching of RhB from aqueous solutions in the presence of TiO2 photocatalyst with LPP system. Properties of generated plasma were investigated by optical emission spectroscopy methods. The results of electrical-discharge degradation of RhB showed that the decomposition rate increased with the applied voltage, pulse width, and frequency. The oxygen gas addition to reactant solution increases the degradation rate by active oxygen species. The RhB decomposition rate was shown to increase with the TiO2 particle dosage. Conclusion: This work presents the conclusions on the photocatalytic oxidation of RhB, as a function of plasma conditions, oxygen gas bubbling as well as TiO2 particle dosage. We knew that using the liquid phase plasma system with TiO2 photocatalyst at high speed we could remove the organic matter in the water.