Background: The aim of this study was to evaluate the physicochemical properties of two newly introduced premixed calcium silicate-based root canal sealers (AH Plus Bioceramic Sealer and Bio-C Sealer) compared to a resin-based root canal sealer (ADseal root canal sealer). Methods: Solubility, pH analysis, calcium ion release, and film thickness of each sealer were evaluated following ISO guidelines. The data were examined using the two-way ANOVA test. Furthermore, X-ray diffraction (XRD) examination was performed to investigate the crystalline phase of each type of sealer. X-ray fluorescence (XRF) analysis was done for the chemical elemental analysis of each sealer. Results: The least film thickness, highest alkalinity, and highest calcium ion release were all displayed by AH Plus Bioceramic Sealer. High solubility, high alkalinity, intermediate calcium ion release, and intermediate film thickness were all displayed by Bio-C Sealer. While ADseal root canal sealer displayed the greatest film thickness, least solubility, alkalinity, and calcium ion release. Conclusions: Both AH Plus Bioceramic Sealer and Bio-C Sealer represented adequate properties to be considered a good sealer that could be used as a potential alternative to resin-based root canal sealers.

Background: Surface microhardness and color stability of dental restorative material should be sustained throughout its functional lifetime to maintain the esthetic quality of the restoration. However, the frequent application of mouthwash may affect their surface microhardness and color stability. The aim of this study was to evaluate the effects of different types of mouthwashes with different contents on surface microhardness and color stability of dental nanohybrid resin-based composite. Methods: Disc specimens of nanohybrid resin composite (Luna Nano-Hybrid Composite) were prepared according to manufacturing instructions; specimens were incubated for 24 h in three types of mouthwash (Chlorohexidine, Listerine Green Tea, and Colgate Optic White Whitening Mouthwash). Artificial saliva was used as a control group. Surface microhardness was evaluated using Vickers microhardness device. Color stability after and before immersion in the different mouthwashes was evaluated using extra-oral spectrophotometer; the values of color change (ΔE₀₀) were subsequently calculated. Data were analyzed using one-way ANOVA and post hoc test (p ≤ 0.05). Results: There was no significant difference between microhardness of resin composite immersed in artificial saliva, CHX, and Green Tea mouthwashes (78.5, 78.4, and 73.5, respectively) (p ≥ 0.1), while the bleaching mouthwash led to the lowest microhardness of resin composite, with significant difference compared to the three previous immersion media (p = 0.002). Moreover, there were significant differences in the color changes (ΔE₀₀) of resin composite exposed to the various immersion media (p = 0.0001). Conclusions: The bleaching mouthwash led to a significant reduction in nanohybrid resin composite’s microhardness compared to the chlorohexidine and Green Tea containing mouthwashes. The resin composite’s color change was accepted in bleaching mouthwash but unaccepted in chlorohexidine and Green Tea containing mouthwashes.

Background: Conventional glass ionomer cements (GICs) are currently the most widely used dental cements due to their chemical bonding into tooth structure, release of fluoride, and ease of manipulation and usage. One of their drawbacks is their low mechanical properties and high solubility. Carbon nanotubes (CNTs) could be utilized in dentistry due to their several potential applications. CNTs can be used as fillers to reinforce polymers or other materials. Additionally, silver (Ag) nanoparticles are highly effective at preventing dental biofilm and enhancing mechanical properties.Objectives: The aim of the present in vitro study is to evaluate the compressive strength, surface microhardness, solubility, and antimicrobial effect of the conventional GIC reinforced with manual blending of 0.01 wt.% Ag doped CNT fillers.Methods: The control group was prepared by mixing dental GIC powder with their liquid. The innovatively reinforced dental GIC group was prepared by incorporating 0.01 wt.% Ag doped CNT fillers into the GIC powder prior to liquid mixing. Chemical characterization was performed by XRF. While, physical characterization was done by measuring film thickness and initial setting time.The compressive strength, surface microhardness, solubility, and antimicrobial effect againstStreptococcus mutansbacteria using an agar diffusion test were measured. The data was statistically analyzed using independent samplet-tests to compare mean values of compressive strength, surface microhardness, solubility, and antimicrobial activity (p ≤ 0.05).Results: The results revealed that innovative reinforced GIC with 0.01 wt.% Ag doped CNT fillers showed higher mean compressive strength, surface microhardness, and antimicrobial effect values than the conventional GIC control group; there was no significant difference between different groups in relation to the solubility test (P ≤ 0.05).Conclusion: The innovatively reinforced GIC with 0.01 wt.% Ag doped CNT fillers had the opportunity to be used as an alternative to conventional GIC dental cements.

Background: Polymethyl methacrylate (PMMA) is used in fabricating acrylic denture bases. Repairing a fractured acrylic denture base can be done by self-cured PMMA, yet this is still a weak point after repair. The aim of this study was to evaluate the effect of incorporating 5% weight titanium oxide nanoparticles (TiO₂) to self-cured PMMA on flexural strength, surface micro-hardness, roughness, and water sorption. Methods: A total of 160 acrylic–resin specimens were used in this study. They were divided in two main groups; (a) control group, prepared by mixing self-cured PMMA powder to its liquid monomer, (b) treated group, prepared by blending 5% weight TiO₂ nanoparticles to self-cured PMMA powder then this blend was mixed with the liquid monomer. Flexure strength, surface micro-hardness, roughness, and water sorption were evaluated. Data were analyzed using independent sample t-tests (p ≤ 0.05). Results: There was a significant increase in the flexural strength of PMMA of the treated group after the addition of TiO₂ (137.6 MPa) compared with the control (75.4 MPa) (p ≤ 0.001). No significant difference between the two groups in terms of micro-hardness (p = 0.385) and surface roughness (p = 0.269). Water sorption showed a significant reduction in the treated group (p ≤ 0.001). Conclusions: Addition of 5% weight TiO₂ nanoparticles to the self-cured acrylic resin improved its flexural strength and reduced its water-sorption without impairing the surface micro-hardness and roughness.

BACKGROUND: Contemporary nickel-titanium (NiTi) rotary endodontic instruments had a revolutionary impact on the success of root canal treatment. AIM: To evaluate the flexibility, microstructure and elemental analysis of four different recent NiTi rotary instruments, namely; Wave One Gold, TF adaptive, HyFlex EDM and Gr_Reciproc Blue compared to conventional Protaper Universal (F2). MATERIAL AND METHODS: The NiTi rotary files were subjected to cantilever bending test to evaluate their flexibility. The microstructural characteristics and elemental analysis were examined via scanning electron microscopy (SEM) and energy dispersive X-ray spectrometer (EDX). RESULTS: The TF adaptive, HyFlex EDM and Wave One Gold endodontic files showed significantly lower cantilever bending values (i.e., higher flexibility) than Protaper F2 and Gr_Reciproc Blue (p < 0.05). The SEM micrographs showed that the bulk of all examined files showed multiple striations due to the cutting process, on the other hand, their external surfaces were different: The Protaper Universal F2 showed multiple voids, while the TF Adaptive surface exhibited more uniform structure. The Hyflex EDM had a crater-like surface, whereas Wave one Gold showed machining grooves with minimum defects, while Reciproc Blue displayed machining grooves with random scratch lines. There was a significant difference in bulk and surface elemental analysis of the various examined files, yet composed mainly of the same elements. CONCLUSION: Chemical composition, heat treatment, manufacturing process and geometrical design of the NiTi rotary instrument have a great influence on their flexibility and microstructure.

Background: Alginate impression is a common dental polymeric material, presented as powder to be mixed with water. Aim: 1. To analyze the effect of alginate powder/water ratio variation on viscosity, tear strength and detail reproduction by in vitro tests, and 2. To evaluate this variation’s effect on patients’ impressions. Materials and methods: Two commercial alginate products were mixed in different viscosities. Viscosity was measured by a viscometer. For the tear strength test, V-shaped specimens were used. For detail reproduction, a die with three scribed lines was used. Clinical dental impressions were examined by stereomicroscope. Results: The alginate specimens mixed with a higher powder/water ratio showed a higher viscosity and tear strength compared to those with a lower powder/water ratio. Both alginate mixtures reproduced two scribed lines in a detail reproduction test. On the other hand, no clear clinical difference was detected when examining dental impressions mixed with a different powder/water ratio. Conclusion: Although increasing the powder/water ratio of mixed alginate raised the resultant viscosity and tear strength by an in vitro test, clinically, no clear difference in tearing was detected. Detail reproduction was minimally affected by the variation in powder/water ratio.