Among the FDM process variables, one of the less addressed in previous research is the filament color. Moreover, if not explicitly targeted, the filament color is usually not even mentioned. Aiming to point out if, and to what extent, the color of the PLA filaments influences the dimensional precision and the mechanical strength of FDM prints, the authors of the present research carried out experiments on tensile specimens. The variable parameters were the layer height (0.05 mm, 0.10 mm, 0.15 mm, 0.20 mm) and the material color (natural, black, red, grey). The experimental results clearly showed that the filament color is an influential factor for the dimensional accuracy as well as for the tensile strength of the FDM printed PLA parts. Moreover, the two way ANOVA test performed revealed that the strongest effect on the tensile strength was exerted by the PLA color (η² = 97.3%), followed by the layer height (η² = 85.5%) and the interaction between the PLA color and the layer height (η² = 80.0%). Under the same printing conditions, the best dimensional accuracy was ensured by the black PLA (0.17% width deviations, respectively 5.48% height deviations), whilst the grey PLA showed the highest ultimate tensile strength values (between 57.10 MPa and 59.82 MPa).

This study examines the effect of elevated printing speeds (100–600 mm/s) on the dimensional accuracy and tensile strength of PLA components fabricated via fused deposition modeling (FDM). To isolate the influence of printing speed, all other parameters were kept constant, and two filament variants—natural (unpigmented) and black PLA—were analyzed. ISO 527-2 type 1A specimens were produced and tested for dimensional deviations and ultimate tensile strength (UTS). The results indicate that printing speed has a marked impact on both geometric precision and mechanical performance. The optimal speed of 300 mm/s provided the best compromise between dimensional accuracy and tensile strength for both filaments. At speeds below 300 mm/s, under-extrusion caused weak layer bonding and air gaps, while speeds above 300 mm/s led to over-extrusion and structural defects due to thermal stress and rapid cooling. Black PLA yielded better dimensional accuracy at higher speeds, with cross-sectional deviations between 2.76% and 5.33%, while natural PLA showed larger deviations of up to 8.63%. However, natural PLA exhibited superior tensile strength, reaching up to 46.59 MPa, with black PLA showing up to 13.16% lower UTS values. The findings emphasize the importance of speed tuning and material selection for achieving high-quality, reliable, and efficient FDM prints.

Dimensional accuracy and mechanical properties of components printed by fused deposition modeling (FDM) are influenced by several process parameters. In this paper, the authors targeted the effect of the printing scenario and the PLA (polylactic acid) color on parts’ quality. Three scenarios were analyzed: individually printing, simultaneously printing of three, respective five specimens of natural (transparent), red, grey, and black PLA. The temperature variations of successive deposited layers were recorded for the black PLA. The dimensional accuracy of tensile specimens was evaluated, tensile tests were performed, and the results were correlated with the mesostructure of the prints. The effect of the independent variables on the measured parameters was analyzed by ANOVA. The experiments revealed differences for the same printing scenario regarding cross-section area (up to 5.71%) and tensile strength (up to 10.45%) determined by the material color. The number of specimens printed simultaneously and the position of the specimens on the build plate were found to influence too, but less than the color. Thus, increasing from one to five the number of specimens printed at a time altered both the dimensional accuracy (up to 3.93% increase of the cross-section area) and the tensile strength (up to 3.63% reduction).

This study examines how manufacturer-specific additive formulations used to obtain nominally identical black PLA filaments influence the thermal, mechanical, and tribological performance of FDM-printed parts. Five commercial filaments were analyzed under identical processing conditions using thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), tensile testing, pin-on-disc measurements, and stereomicroscopy. The filaments exhibited substantial compositional variability, with total additive contents ranging from 2.08 wt.% to 27.82 wt.%. One filament (M5) contained a significant fraction of inorganic fillers, confirmed by SEM/EDX as Ca-, Na- and Mg-based oxides and silicates, identifying it as a PLA-based composite despite being marketed as standard PLA. These differences strongly affected thermal behavior (Tg, Tcc, Tm) and translated directly into the performance of the printed parts. Ultimate tensile strength varied by 88.91% across all filaments (19.38–36.61 MPa), but only by 13% among the four conventional PLA filaments (M1–M4). Tribological performance differed markedly: mean coefficients of friction ranged from 0.246 (M3) to 0.368 (M2), a spread of approximately 50%, with wear-track morphologies reflecting the frictional response. Overall, the results show that PLA filaments cannot be treated as interchangeable materials. Greater transparency and standardized reporting of filament composition are needed to ensure reproducibility and support informed material selection in FDM applications.

The study investigates the influence of infill density on the dimensional and geometric deviations of Polylactic Acid (PLA) cubic specimens manufactured using Fused Deposition Modeling (FDM). Five infill levels (20–100%) were analyzed, while all other process parameters were kept constant. Flatness, parallelism, perpendicularity, and dimensional measurements were performed using a Mitutoyo MiSTAR 555 coordinate measuring machine, providing micron-level accuracy. The results show that infill density has selective and direction-dependent effects on geometric accuracy, without indicating a general trend applicable to all types of deviations. A linear increase in printing time and specimen mass was also observed as infill density increased, indicating a direct impact on manufacturing cost.