The growing demand for concrete in tropical regions faces two unresolved challenges: the high carbon footprint of ordinary Portland cement (OPC) and limited understanding of how supplementary cementitious materials affect the mechanical performance of laterite rock aggregates concrete. Although metakaolin (MK) is a highly reactive pozzolan, its combined use with laterite rock aggregates concrete and its influence on strength development and microstructure have not been sufficiently clarified. This study investigates the mechanical behavior and sustainability potential of laterite rock aggregate concrete in which OPC is partially replaced by MK at 0%, 5%, 10%, 15%, and 20% by weight. All mixes were prepared at a constant water–binder ratio of 0.50 and tested for workability, compressive strength, split-tensile strength, and flexural strength at 7, 14, and 28 days, with and without a polycarboxylate-based superplasticizer. The results show that MK significantly enhances the mechanical performance of laterite rock concrete, with an optimum at 10% replacement: the 28-day compressive strength increased from 35.6 MPa (control) to 53.9 MPa in the superplasticized mix, accompanied by corresponding gains in tensile and flexural strengths. SEM–EDS analyses revealed microstructural densification, reduced portlandite, and a refined interfacial transition zone, explaining the improved strength and cracking resistance. From an environmental perspective, a 10% MK replacement corresponds to an approximate 10% reduction in clinker-related CO₂ emissions, while the use of locally available laterite rock reduces the dependence on quarried granite and transportation impacts. The findings demonstrate that MK-modified laterite rock concrete is a viable and eco-efficient option for structural applications in tropical regions. The study concludes that MK-enhanced laterite rock aggregate concrete can deliver higher structural performance and improved sustainability without altering conventional mix design and curing practices.

This study investigates the combined use of waste glass cullet (WGC) and snail shell powder (SSP) as a sustainable binary cementitious system to enhance the mechanical performance and durability of concrete, particularly for rigid pavement applications. Nine concrete mixes were formulated: a control mix, four mixes with 5%, 10%, 15%, and 20% WGC as partial cement replacement, and four corresponding mixes with 1% SSP addition. Slump, compressive strength, and flexural strength were evaluated at various curing ages. Results showed that while WGC reduced workability due to its angular morphology (slump decreased from 30 mm to 20 mm at 20% WGC), the inclusion of SSP slightly mitigated this reduction (21 mm at 20% WGC + 1% SSP). At 28 days, compressive strength increased from 40.0 MPa (control) to 45.0 MPa with 20% WGC and further to 48.0 MPa with the addition of SSP. Flexural strength also improved from 7.0 MPa (control) to 7.8 MPa with both WGC and SSP. These improvements were statistically significant (p < 0.05) and supported by correlation analysis, which revealed a strong inverse relationship between WGC content and slump (r = −0.97) and strong positive correlations between early and later-age strength. Microstructural analyses (SEM/EDX) confirmed enhanced matrix densification and pozzolanic activity. The findings demonstrate that up to 20% WGC with 1% SSP not only enhances strength development but also provides a viable, low-cost, and eco-friendly alternative for producing durable, load-bearing, and sustainable concrete for rigid pavements and infrastructure applications. This approach supports circular economic principles by valorizing industrial and biogenic waste streams in civil construction.