This research investigated the effect of fly ash content on the compressive strength development of ultra-high-performance concrete (UHPC) at different curing conditions, i.e., the standard curing condition and the heat curing. A total of 20 mixtures were prepared to cast specimens to measure the compressive strength at different ages from 3 days to 180 days. Additionally, 300 specimens were prepared to estimate the appropriate heat curing period at the early ages in terms of enhancing the 28-day compressive strength of UHPC with high content of fly ash (FA). From the regression analysis using test data, empirical equations were formulated to assess the compressive strength development of UHPC considering the FA content and maturity function. Test results revealed that the preference of the addition of FA for enhancing the compressive strength of UHPC requires the early heat curing procedure which can be recommended as at least 2 days under 90 °C. Moreover, the compressive strength of UHPC with FA under heat curing mostly reached its 28-day strength within 3 days. The proposed models based on the fib 2010 model can be a useful tool to reliably assess the compressive strength development of UHPC with high-volume fly ash (HVFA) (up to 70% fly ash content) under a heat curing condition that possesses a different performance from that of normal- and high-strength concrete. When 50% of the cement content was replaced by FA, the embodied CO₂ emission for UHPC mixture reduced up to approximately 50%, which is comparable to the CO₂ emission calculated from the conventional normal-strength concrete.

This study examined the effectiveness of zeolite addition to reduce the autogenous shrinkage of high-performance cement-based concrete (HPC). The zeolites were replaced up to 15% of the cement content by weight and their mean particle size varied from 5.6 to 16.7 µm. To evaluate the crack resistance of HPC containing zeolites, the ring tests and internal relative humidity measurements were performed at different ages. The compressive strengths were determined at 3, 7, 28 and 90 days of curing. Test results confirmed that the addition of zeolite was promising and favourable in enhancing the compressive strength, crack resistance and reducing the autogenous shrinkage of HPC due to synergistic pozzolanic and internal curing effects. The autogenous shrinkage tended to decrease with the increase in zeolite content and its particle size. In addition, the extent of the autogenous shrinkage development at the early ages decreased with higher zeolite content replaced. Furthermore, to predict the autogenous shrinkage of HPC containing zeolite, an improved model has been proposed, in which the conventional ultimate autogenous shrinkage strain and time function were modified by introducing new parameters accounting for the zeolite content and its particle size. It appeared that the proposed model was able to capture the autogenous shrinkage behaviour of HPC with or without zeolite, while the fib 2010 model underestimated the autogenous shrinkage of HPC containing less than 10% zeolite replacement.