Enamel demineralization around orthodontic adhesive is a common esthetic concern during orthodontic treatment. The aim of this study was to prepare orthodontic adhesives containing monocalcium phosphate monohydrate (MCPM) and nisin to enable mineralizing and antibacterial actions. The physicomechanical properties and the inhibition of S. mutans growth of the adhesives with added MCPM (5, 10 wt %) and nisin (5, 10 wt %) were examined. Transbond XT (Trans) was used as the commercial comparison. The adhesive containing a low level of MCPM showed significantly higher monomer conversion (42–62%) than Trans (38%) (p < 0.05). Materials with additives showed lower monomer conversion (p < 0.05), biaxial flexural strength (p < 0.05), and shear bond strength to enamel than those of a control. Additives increased water sorption and solubility of the experimental materials. The addition of MCPM encouraged Ca and P ion release, and the precipitation of calcium phosphate at the bonding interface. The growth of S. mutans in all the groups was comparable (p > 0.05). In conclusion, experimental orthodontic adhesives with additives showed comparable conversion but lesser mechanical properties than the commercial material. The materials showed no antibacterial action, but exhibited ion release and calcium phosphate precipitation. These properties may promote remineralization of the demineralized enamel.

Dental caries is a major oral health problem, which associates with cariogenic bacteria. Streptococcus mutans and Lactobacillus acidophilus are facultative anaerobic bacteria that are found in tooth decay. Accordingly, neem leaf extract was developed due to its great anti-microbial property against many bacteria. The aim of this study was to determine anti-cariogenic properties of neem leaf extract in a novel paste preparation. The neem extract was derived from maceration of dry neem leaves in ethanol for 48 h. The ethanolic extract was subjected to chemical identification using GC-MS. Neem pastes were prepared from ethanolic extract mixed with polyethylene glycol paste with or without zinc oxide. S. mutans and L. acidophilus test were initiated at bacterial concentration of 108 CFU/ml. The antibacterial activity was then performed by disc diffusion method following by minimum bactericidal concentration (MBC) technique. GC-MS result displayed 35 compounds. Compounds found in the extract were n-Hexadecanoic acid (31.18%), Hentriacontane (18%), Phytol (16.79%). Disc diffusion showed that ethanolic extract and neem pastes inhibited growth of both bacteria. For MBC, neem paste with zinc oxide at concentration of neem 0.4 mg/ml was the most effective concentration on inhibiting S. mutans growth. Neem pastes and ethanolic extract at concentration of neem 6.25 mg/ml inhibited L. acidophilus growth. The ethanolic neem leaf extract and novel neem pastes had antimicrobial effect on both S. mutans and L. acidophilus. By this property, neem paste could be developed for the application in dental field, i.e. pulp capping. Key words:Neem, Azadirachta indica, antimicrobial, cariogenic bacteria.