Direct metal laser deposition (DMLD) is an additive manufacturing technique suitable for coating and repair, which has been gaining a growing interest in 3D manufacturing applications in recent years. However, its diffusion in the manufacturing industry is still limited due to technical challenges to be solved—both the sub-optimal quality of the final parts and the low repeatability of the process make the DMLD inadequate for high-value applications requiring high-performance standards. Thus, real-time monitoring and process control are indispensable requirements for improving the DMLD process. The aim of this study was the optimization of deposition strategies for the fabrication of thin walls in AISI 316L stainless steel. For this purpose, a coaxial monitoring system and image processing algorithms were employed to study the melt pool geometry. The comparison tests carried out highlighted how the region-based active contour algorithm used for image processing is more efficient and stable than others covered in the literature. The results allowed the identification of the best deposition strategy. Therefore, it is shown how this monitoring methodology proved to be suitable for designing and implementing the right building strategy for DMLD manufactured 3D components. A fast and stable image processing method was achieved, which can be considered for future closed-loop monitoring in real-time applications.

The capabilities of additive manufacturing (AM) techniques have been extensively examined in the literature. However, scientific gaps persist on the feasibility of realizing a coated component manufactured by using various materials processed by combining different AM processes. From this perspective, this study focuses on the manufacturing of a directed energy deposition (DED) coating by using 18Ni (300) maraging steel powder on AISI 316L components realized by laser-powder bed fusion (L-PBF), in order to assess the production of components with high geometrical complexity combined with high mechanical surface properties in selected areas. The quality of the manufactured coatings was assessed in-process through the implementation of an optical monitoring system and real-time image processing. In addition, an in-depth metallurgical analysis (microstructural and chemical) of the interface between the DED coating and the L-PBF component was carried out. Finally, hardness tests were performed on both the as-deposited and heat-treated coatings to confirm the high mechanical performance of the final component surface. The results revealed the potential of producing cost-effective and geometrically complex parts, such as molds or tools with internal cooling channels, that implement mechanically high-performance surfaces.

The main objective of this study is to evaluate residual stresses in AISI 316L and 18Ni Maraging 300 functionally graded materials with continuous variation of composition within a single layer using the contour method. The manufacture of this kind of layer-level continuous functionally graded materials by employing a Powder Bed Fusion-Laser Beam system utilizing a blade/roller-based powder spreading technique has only been recently devised and a proper residual stress analysis is still required. In fact, as the mechanical properties of additively manufactured samples are significantly influenced by the direction of construction, the same holds true for the direction along which the compositional variation is made. Furthermore, in this study, the impact of solution annealing and aging heat treatment, which are necessary for enhancing the mechanical properties of martensitic steel, on residual stresses was explored. Additionally, the effect of adopting material-differentiated process parameters was investigated. The results indicated that each specimen displayed areas of tensile stress concentration on the upper and lower surfaces, balanced by compression in the center. The application of heat treatment led to a decrease in the maximum tensile stress of 8% and provided a uniform and significant stress reduction within the maraging steel. Finally, the implementation of material-specific process parameters for the three composition zones in conjunction with the heat treatment resulted in a reduction in the maximum residual stress of 35% and also a significantly lower residual stress field throughout the specimen.