Using thermal storage materials with excellent thermal properties in the energy utilization system enables efficient use of renewable energy sources. Organic phase change materials (PCMs) have the advantages of high heat storage density, no corrosion, and low cost, but low thermal conductivity and insufficient heat transfer capacity have always been the bottlenecks in their application. In this paper, melamine foam@ reduction graphene oxide (MF@rGO) and carbon foam@ reduction graphene oxide (CF@rGO) composite foams with double carbon networks were prepared by self-assembly method and further employed in 1-octadecinal (OD) PCMs. The microstructure, chemical composition, phase change behavior, thermal conductivity, and photothermal conversion performance of MF@rGO/OD and CF@rGO/OD were studied in detail using SEM, FTIR, Raman DSC, and LFA. The melting and solidification enthalpies of CF@rGO/OD composite PCMs were 208.3 J/g and 191.4 J/g, respectively, its thermal conductivity increased to 1.54 W/m·K, which is 6.42 times that of pure OD. The porous structure and high thermal conductivity of the double carbon network substantially enhance the efficiency of energy storage and release in composite PCMs. CF@rGO/OD composite PCMs have excellent heat storage performance and heat transfer capacity, and a wide range of application prospects in the fields of low-temperature solar heat storage, precision instrument temperature control, and intelligent buildings.

Multiform NiO nanowalls with a high specific surface area were constructed in situ on carbon foam (CF) to construct NiO@CF/OD composite phase change materials (CPCMs). The synthesis mechanism, microstructures, thermal management capability, and photothermal conversion of NiO@CF/OD CPCMs were systematically studied. Additionally, the collaborative enhancement effects of CF and multiform NiO nanowalls on the thermal properties of OD PCMs were also investigated. NiO@CF not only maintains the porous 3D network structure of CF, but also effectively prevents the aggregation of NiO nanosheets. The chemical structures of NiO@CF/OD CPCMs were analyzed using XRD and FTIR spectroscopy. When combined with CF and NiO nanosheets, OD has high compatibility with NiO@CF. The thermal conductivity of NiO@CF/OD-L CPCMs was 1.12 W/m·K, which is 366.7% higher than that of OD. The improvement in thermal conductivity of CPCMs was theoretically analyzed according to the Debye model. NiO@CF/OD-L CPCMs have a photothermal conversion efficiency up to 77.6%. This article provided a theoretical basis for the optimal design and performance prediction of thermal storage materials and systems.

Solid–liquid phase-change materials (PCMs) have attracted considerable attention in heat energy storage due to their appropriate phase-transition temperatures and high thermal storage density. The primary issues that need to be addressed in the wide application of traditional PCMs are easy leakage during solid–liquid phase transitions, low thermal conductivity, and poor energy conversion function. The heat transfer properties of PCMs can be improved by compounding with carbon materials. Carbon nanotubes (CNTs) are widely used in PCMs for heat storage because of their high thermal conductivity, strong electrical conductivity, and high chemical stability. This study investigates the thermal properties of 1-octadecanol (OD) modified with different diameters and amounts of CNTs using the melt blending method and the ultrasonic dispersion method. The aim is to enhance thermal conductivity while minimizing latent heat loss. The physical phase, microstructure, phase-change temperature, phase-transition enthalpy, thermal stability, and thermal conductivity of the OD/CNTs CPCMs were systematically studied using XRD, FTIR, SEM, DSC, and Hot Disk. Moreover, the heat charging and releasing performance of the OD/CNTs CPCMs was investigated through heat charging and releasing experiments, and the relationship among the composition–structure–performance of the CPCMs was established.

The rapid expansion of the renewable energy industry renders thermal energy storage technology a critical support for high-efficiency energy utilization. As an organic phase change material (PCMs), 1-octadecanol (OD) is plagued by intrinsic limitations of low thermal conductivity and sluggish heat absorption release kinetics, restricting its practical deployment under high-power thermal energy storage operating conditions. In this study, carbon nanotubes (CNTs), graphene (GR) and three-dimensional carbon foam (CF) were utilized to modify OD for fabricating a series of composite phase change thermal storage materials (CPCMs). A suite of characterizations including FTIR, SEM, DSC, and Hot Disk measurements were employed to systematically probe the phase composition, microstructure, phase change temperature, phase change enthalpy, stability, and thermal conductivity of CPCMs. Modification effects exerted by carbon-based fillers with varied structures on OD differ remarkably. Three-dimensional network structured CF can effectively build continuous thermal conduction pathways, while GR sheets contribute to optimized interfacial heat transfer performance. In contrast, CNTs are prone to agglomeration and intertwining, which undermines their thermal conductivity enhancement effect. Nevertheless, all CPCMs retain favorable thermal storage capability and superior cycling stability. This work provides meaningful guidance for the rational selection of carbon-based fillers and performance optimization of low-temperature organic PCMs.