To analyze the association of several types of malignant lymphomas in different anatomical sites with the Epstein-Barr virus (EBV) infection status, 127 cases of formalin-fixed paraffin-embedded samples of malignant lymphomas were investigated with in situ hybridization detecting EBV-encoded small RNA (EBER) in tumor cells. Forty-six out of 108 non-Hodgkin lymphoma (NHL) cases were positive for EBER (42.6%). The EBER-positivity rate of NHL in the nasal cavity and nasopharynx (35/60 cases, 58.3%) was higher than that of NHL in stomach (9/30 cases, 30%) and in the superficial lymph nodes (2/18 cases, 11.1%) (P<0.05). The EBER-positivity rate of Hodgkin lymphoma in the superficial lymph nodes was 26.3% (5/19 cases). These findings suggest that the EBV-positivity rate in lymphomas is related to their histological types and locations.

Cement emulsified asphalt mortar (CA) is widely used as the cushion of two types of ballastless track (CRTS I and CRTS II) in high-speed railways. Nowadays, the lack of durability of CA mortar has severely affected the quality of high-speed railways, failing to meet the requirements of sustainability. Since CA mortar is a kind of porous material, its performance can be significantly affected by its microstructures, which means that revealing the evolution law of its microstructures can provide the basis for improving its durability. Therefore, CA mortar species with different asphalt-cement ratio under different curing ages were prepared based on the requirements of CRTS II in this research and the pore structures were determined based on SEM and NMR methods. Then, a fractal model of CA mortar pore volume was proposed based on the concept of box fractal dimension, and the fractal dimension of pore volume was calculated. The relationship between fractal dimensions and mechanical property was analyzed based on Pearson correlation coefficient and regression analysis. The results suggested that the overall microstructure of CA mortar shows a loose porous space structure with cement hydration products being the continuous phase and asphalt being the dispersed phase. With the increase in A/C ratio, the hydration products produced by cement hydration decrease, and the total porosity and average porosity of CA mortar gradually increase due to the increase of asphalt hindering the hydration process of the cement. With the increase in curing age, the pore structure of CA mortar becomes more compact. However, the evolution law of CA mortar pore structure with age is not consistent under different A/C ratios due to the influence of asphalt. The pore structure of CA mortar was proved to have obvious fractal characteristics based on the concept of box fractal dimension and the experimental data of NMR. In addition, the correlation analysis proves that the fractal dimension of pore structure has an obvious positive correlation with the compressive and flexural strength, which suggests that the fractal dimension of pore volume can be a bridge for connecting the macro-property and micro-structures of CA mortar.

Cement-emulsified asphalt mortar (CA mortar) is an organic–inorganic composite material composed of cement, emulsified asphalt, fine sand, water, and various admixtures. It is mainly used as the cushion layer for high-speed railway ballastless tracks. CA mortar cushion layers in North China often have to withstand the coupling effects of humidity and freeze–thaw, which has a very important impact on the fatigue performance of CA mortar. Based on the big data statistical results, the temperature conditions and cycle times of the CA mortar layer Freeze–Thaw cycle in North China were determined. Also, a fatigue performance test under humidity–freeze–thaw coupling conditions was designed and carried out. The fitting curve equations of fatigue stress and fatigue life under different humidity conditions and freeze–thaw coupling were established. The relationship between fatigue performance parameters K and n and humidity conditions was analyzed. This study shows that with the increase in humidity, the fatigue life of CA mortar under different humidity conditions shows an overall downward trend. The fatigue performance and fatigue life stress level sensitivity of CA mortar decrease with increasing humidity. The proportion of water damage and freeze–thaw damage to total damage increases with increasing humidity, which means that the humidity and freeze–thaw have a more significant impact on the fatigue properties of CA mortar. When the humidity is low, the fatigue cracks of CA mortar are mostly generated across the cement paste, and the macroscopic damage presents as longitudinal cracking. When the humidity is high, the fatigue cracks of CA mortar are mostly generated at the interface between aggregate and paste, and the macroscopic damage presents as oblique cracking. Based on the analysis of the damage mechanism, it is suggested that the humidity of CA mortar should be controlled below 25% in the actual project to ensure its durability.