Titanium (Ti) and its alloys offer favorable biocompatibility, mechanical properties and corrosion resistance, which makes them an ideal material choice for dental implants. However, the long-term success of Ti-based dental implants may be challenged due to implant-related infections and inadequate osseointegration. With the development of nanotechnology, nanoscale modifications and the application of nanomaterials have become key areas of focus for research on dental implants. Surface modifications and the use of various coatings, as well as the development of the controlled release of antibiotics or proteins, have improved the osseointegration and soft-tissue integration of dental implants, as well as their antibacterial and immunomodulatory functions. This review introduces recent nano-engineering technologies and materials used in topographical modifications and surface coatings of Ti-based dental implants. These advances are discussed and detailed, including an evaluation of the evidence of their biocompatibility, toxicity, antimicrobial activities and in-vivo performances. The comparison between these attempts at nano-engineering reveals that there are still research gaps that must be addressed towards their clinical translation. For instance, customized three-dimensional printing technology and stimuli-responsive, multi-functional and time-programmable implant surfaces holds great promise to advance this field. Furthermore, long-term in vivo studies under physiological conditions are required to ensure the clinical application of nanomaterial-modified dental implants.

Background: Computer-aided design and computer-aided manufacturing (CAD-CAM) materials for prosthetic is gaining popularity in dentistry. However, limited information exists regarding the impact of thickness and roughening treatment on the optical properties of contemporary CAD-CAM restorative materials. This study aimed to quantitatively evaluate the translucency and opalescence of six dental CAD-CAM materials in response to different thicknesses and roughening treatments. Methods: Six dental CAD-CAM materials, lithium disilicate glass–ceramic (IPS e.max CAD, LS), polymer-infiltrated ceramic (VITA Enamic, VE), resin-nano ceramic glass–ceramic (LAVA Ultimate, LU), polymethyl methacrylate (Telio CAD, TE), and two zirconia reinforced lithium silicate (VITA Suprinity, VS, and Celtra Duo, CD), in shade A2 were prepared as 12 × 12mm² specimens of four thicknesses (0.5mm, 1.0mm, 1.5mm, and 2.0mm) (N = 240, n = 10). After three different treatments (polished, roughened by SiC P800-grit, and SiC P300-grit), the translucency parameter (TP₀₀) and opalescence parameter (OP) were measured with a spectrophotometer (VITA Easyshade V). The surface roughness was analyzed with a shape measurement laser microscope. The data were analyzed using a MANOVA, post hoc Tukey–Kramer test, the t test, and regression analysis (α = .05). Results: The TP₀₀ and OP were significantly influenced by material type, thickness and roughening treatment (P < .05). TP₀₀ showed a continues decline with increasing thicknesses, while the variations of OP were material-dependent. TP₀₀ ranged from 37.80 (LS in 0.5mm) to 5.66 (VS in 2.0mm), and OP ranged from 5.66 (LU in 0.5mm) to 9.55 (VS in 0.5mm). The variations in TP₀₀ of all materials between adjacent thicknesses ranged from 2.10 to 15.29, exceeding the acceptable translucency threshold except for LU. Quadratic and logarithmic regression curves exhibited the best fit for TP₀₀ among the materials. Compared to polished specimens, rougher specimens exhibited lower TP00 and higher OP in all materials except for LS (P < 0.05). Roughening with P300-grit decreased TP₀₀ and OP by an average of 2.59 and 0.43 for 0.5mm specimens, and 1.26 and 0.25 for 2.0mm specimens, respectively. Conclusions: Variations in translucency caused by thickness and roughening treatment were perceptible and may be clinically unacceptable. Careful consideration should be given to the selection of CAD-CAM materials based on their distinct optical properties.

The regenerative treatment of infectious vertical bone defects remains difficult and challenging today. Current clinical treatments are limited in their ability to control bacteria and infection, which is unfavorable for new bone formation and calls for a new type of material with excellent osteogenic and antibacterial properties. Here a multifunctional scaffold is synthesized that mimics natural bone nanostructures by incorporating silver nanowires into a hierarchical, intrafibrillar mineralized collagen matrix (IMC/AgNWs), to achieve the therapeutic goals of inhibiting bacterial activity and promoting infectious alveolar bone augmentation in rats and beagle dogs. An appropriate concentration of 0.5 mg mL⁻¹ AgNWs is selected to balance biocompatibility and antibacterial properties. The achieved IMC/AgNWs exhibit a broad spectrum of antimicrobial properties against Gram‐negative Porphyromonas gingivalis and Gram‐positive Streptococcus mutans. When the IMC/AgNWs are cocultured with periodontal ligament stem cells, it possesses excellent osteoinductive activities under both non‐inflammatory and inflammatory conditions. By constructing a rat mandibular infected periodontal defect model, the IMC/AgNWs achieve a near‐complete healing through the canonical BMP/Smad signaling. Moreover, the IMC/AgNWs enhance vertical bone height and osseointegration in peri‐implantitis in beagle dogs, indicating the clinical translational potential of IMC/AgNWs for infectious vertical bone augmentation.