The surface and subsurface conditions of components are critical for their functional properties. Every manufacturing process modifies the surface condition as a consequence of its mechanical, chemical, and thermal impact or combinations of the three. The depth of the affected zone varies for different machining operations and is related to the process parameters and characteristics. Furthermore, the initial material state has a decisive influence on the modifications that lead to the final surface conditions. With this knowledge, the collaborative research center CRC/Transregio 136 “Process Signatures” started a first joint investigation to analyze the influence of several machining operations on the surface modifications of uniformly premanufactured samples in a broad study. The present paper focusses on four defined process chains which were analyzed in detail regarding the resulting surface conditions as a function of the initial state. Two different workpiece geometries of the same initial material (AISI 4140, 42CrMo4 (1.7225) classified according to DIN EN ISO 683-2) were treated in two different heat treating lines. Samples annealed to a ferritic-perlitic microstructure were additionally deep rolled as starting condition. Quenched and tempered samples were induction hardened before further process application. These two states were then submitted to six different manufacturing processes, i.e., grinding (with mainly mechanical or thermal impact), precision turning (mainly mechanical), laser processing (mainly thermal), electrical discharge machining (EDM, mainly thermal) and electrochemical machining (ECM, (mainly chemical impact). The resulting surface conditions were investigated after each step of the manufacturing chain by specialized analysis techniques regarding residual stresses, microstructure, and hardness distribution. Based on the process knowledge and on the systematic characterizations, the characteristics and depths of the material modifications, as well as their underlying mechanisms and causes, were investigated. Mechanisms occurring within AISI 4140 steel (42CrMo4) due to thermal, mechanical or mixed impacts were identified as work hardening, stress relief, recrystallization, re-hardening and melting, grain growth, and rearrangement of dislocations.

The functional properties of a workpiece are determined by a modification of the surface and subsurface materials. In this work, the correlation between thermo-mechanical material loads and the modification of the residual stresses is presented. While the resulting residual stresses were measured by X-ray diffraction after machining experiments, the material loads were determined using a process simulation. The experimental data (measured process forces and results from previous experiments) are used to validate the simulation, which is then applied to calculate the internal thermo-mechanical loads of the maximal temperature and the equivalent von-Mises-stresses per volume element during the machining experiments. In conclusion, a higher depth impact of mechanical loads compared to a lower depth impact of thermal loads in precision machining is observed. For the sake of novelty, the thermo-mechanical loads were plotted and interpreted in a three-dimensional fashion. Finally, cross sections of this mutual representation at certain constant material loads—thermal and mechanical—result in a process signature, which can prospectively improve the prediction of functional workpiece properties.

The loads acting on a workpiece during machining processes determine the modification of the surface of the final workpiece and, thus, its functional properties. In this work, a method that uses thermocouples to measure the temperature in precision fly-cutting machining with high spatial and temporal resolution is presented. Experiments were conducted for various materials and machining parameters. We compare experimental measurement data with results from modern and advanced machining process simulation and find a good match between experimental and simulation results. Therefore, the simulation is validated by experimental data and can be used to calculate realistic internal loads of machining processes.

For bulk material it is very well known, that the material properties differ between the material near the surface and the inner material (i.e. segregations). However, for sheet material a gradient of material properties in depth direction and its influence on forming processes was not yet investigated. Within experiments on sheet steel 1.0338 (DC04) a gradient in material properties was proven by hardness measurements for both unprocessed material as well as after conducting forming and milling processes. The characterisation shows a gradient in material hardness over the entire sheet thickness. The experimental results regarding forming processes, such as rolling and bending, additionally show an increase of the materials hardness due to work hardening. The problem from the inhomogeneous material properties leads to an inaccurate prediction of the forming behaviour of the workpiece in further processing. Machining experiments were conducted for transferring the knowledge of modified surface and subsurface layers onto forming processes and their simulation. The bending experiments and the corresponding process simulation of the spring back behaviour show, that the implementation of an inhomogeneous material property increases the prediction accuracy. Notably the prediction of the spring back behaviour of thinner sheet metals is highly improved. Therefore, an analysis of sheet metal properties in thickness direction and their consideration in forming process simulations is inevitable for the implementation of accurate material models.