The transition toward circular economy models has been progressively promoted in the last few years. Different disciplines and strategies may significantly support this change. Although the specific contribution derived from design, material science, and additive manufacturing is well-established, their interdisciplinary relationship in circular economy contexts is relatively unexplored. This paper aims to review the main case studies related to new circular economy models for waste valorization through extrusion-based additive manufacturing, circular materials, and new design strategies. The general patterns were investigated through a comprehensive analysis of 74 case studies from academic research and design practice in the last six-year period (2015–2021), focusing on the application fields, the 3D printing technologies, and the materials. Further considerations and future trends were then included by looking at the relevant funded projects and case studies of 2021. A broader number of applications, circular materials, and technologies were explored by the academic context, concerning the practice-based scenario linked to more consolidated fields. Thanks to the development of new strategies and experiential tools, academic research and practice can be linked to foster new opportunities to implement circular economy models.

Within the complex framework of additive manufacturing, direct ink writing (DIW) processes significantly contribute to extending the range of 3D‐printable materials (i.e., thermosetting resins, ceramics, hydrogels). Thanks to this technology, viscous inks are easily extruded for the creation of 3D structures. Nevertheless, the quick recovery of the solid‐like behavior after extrusion remains one of the most crucial open issues for 3D‐printable inks. The main goal herein is to improve the printability of a UV‐curable thermosetting composite ink reinforced with mechanically recycled glass fiber composites by modifying its rheological behavior. The overall process is optimized, leading to the definition of the optimal extrusion parameters for these types of materials. Furthermore, the retraction mode is successfully developed for the DIW of recycled composites. Additional features are achieved, thanks to the aforementioned improvements, such as 3D complex shapes, assembled pieces, and/or moving built‐in mechanisms, increasing the number of new potential applications of recycled glass fiber‐reinforced polymers.

Despite the growing global interest in 3D printed carbon fiber reinforced polymers, most of the applications are still limited to high-performance sectors due to the low effectiveness–cost ratio of virgin carbon fibers. However, the use of recycled carbon fibers in 3D printing is almost unexplored, especially for thermoset-based composites. This paper aims to demonstrate the feasibility of recycled carbon fibers 3D printing via UV-assisted direct ink writing. Pyrolyzed recycled carbon fibers with a sizing treatment were firstly shredded to be used as a reinforcement of a thermally and photo-curable acrylic resin. UV-differential scanning calorimetry analyses were then performed to define the material crosslinking of the 3D printable ink. Because of the poor UV reactivity of the resin loaded with carbon fibers, a rheology modifier was added to guarantee shape retention after 3D printing. Thanks to a customized 3D printer based on a commercial apparatus, a batch of specimens was successfully 3D printed. According to the tensile tests and Scanning Electron Microscopy analysis, the material shows good mechanical properties and the absence of layer marks related to the 3D printing. These results will, therefore, pave the way for the use of 3D printed recycled carbon fiber reinforced polymers in new fields of application.

Food waste and loss generate significant waste such as spent coffee grounds (SCGs) from coffee consumption. These byproducts can be valorized by following circular economy and bioeconomy principles, e.g., using SCGs in polymer-based composites for 3D printing. Although desktop-size material extrusion additive manufacturing is increasingly adopted for biomass-polymer-based composites, the potential of large-format direct extrusion 3D printing systems remains unexplored. This work investigated the thermal, rheological, and mechanical properties of PLA/SCG composites for applications with a large-format pellet extrusion 3D printer. The formulations exhibit minimal degradation at typical 3D printing temperatures of PLA, i.e., ∼190 °C, and limited effects on crystallinity by increasing the SCG weight percentage. The decrease in viscosity due to SCGs improves the printability and layer adhesion, as confirmed by the tensile test results, such as higher ultimate tensile strength and elongation at break values compared to those of the state-of-the-art values. Using pellet feedstocks contributes to limiting the effects of thermomechanical degradation by reducing raw material processing, i.e., avoiding filament extrusion. Using PLA/SCGs formulations was demonstrated through 3D printed complex parts with nonplanar slicing techniques, including a large-scale furniture product, validating large-format pellet extrusion 3D printers for scaling up the use of biomass-filled polymers.