Iron ore pellet reduction experiments were performed with pure hydrogen (H₂) and mixtures with carbon monoxide (CO) at different ratios. For direct reduction processes that switch dynamically between reformed natural gas and hydrogen as the reductant, it is important to understand the effects of the transition on the oxide reduction kinetics to optimize the residence time of iron ore pellets in a shaft reactor. Hence, the reduction rates were studied by varying experimental parameters such as the temperature (800, 850 & 900 °C), reactant gas flow rate (100, 150 & 200 cm³/min), pellet size and composition of the reactant gas mixture. The rate of reduction was observed to increase with an increase in temperature and reactant gas flow rate, but it decreased with an increase in pellet size. SEM greyscale analysis was performed to analyze the porosity and phase composition of partially reduced pellets. The porosity of the pellets was observed to increase from 0.3 for unreacted pellet to 0.42 for a completely reduced pellet. Energy-dispersive X-ray spectroscopy (EDAX) analysis was performed to identify the phases observed in the SEM images. The fraction of iron phase was observed to increase from the shell region of the pellet to the core region with an increase in the degree of reduction. A 2D-axisymmetric numerical model was developed on COMSOL Multiphysics, and it was validated using the conversion (X) vs. time curves obtained from each experiment. The model was able to accurately predict the total time needed for the complete conversion of a single iron ore pellet for multiple experiments. Effects of changes in the porosity and tortuosity of the pellet on the model were also studied and the rate of reduction was observed to be sensitive to changes in both porosity and tortuosity. The SEM analysis and the model results show that tortuosity is higher for pellets reduced with H₂ than for pellets reduced with H₂-CO gas mixtures.

Direct reduction of hematite pellets with hydrogen (H₂) was used to produce directly reduced iron (DRI) in a pilot scale reactor at a pellet feed rate of 21.4 kg/h. At a steady state, operational parameters of the pilot plant (gas recycling rate and inlet temperature) along with key reactor output parameters, the pellet metallization, and the internal temperature profile of the reactor were reported for two scenarios with high recycle and low recycle rate of H₂. Scenario 1, with a high recycle rate of 400 L/min H₂ along with external heating of 870 °C, gave an average metallization of 91.8%, while Scenario 2, with low recycle rate of 100 L/min H₂ and external heating of 850 °C gave a metallization of 67.8% due to the higher moles of H₂ available for reduction and the external energy required for the endothermic reduction reaction in Scenario 1 as compared with Scenario 2. Finite element analysis was used to build a model of the shaft reactor, which was validated against the metallization and internal temperature profile data. The average metallization values predicted by the model were very close to the metallization values obtained from the pilot plant samples, with 90.9% average metallization for Scenario 1 and 65.6% average metallization for Scenario 2. The internal temperature profiles in the lower region of the reactor obtained from the model were very close to these pilot plant data, with a maximum difference of 52.7 °C and 67.6 °C for Scenarios 1 and 2, respectively. The pilot plant reactor model was used extensively in the commissioning of the pilot plant and to predict the startup outcomes for a given set of operating parameters.