High-entropy herringbone alloy: Eutectic high-entropy alloys have a dual phase structure that could be useful for optimizing a material’s properties. Shi et al . found that directional solidification of an aluminum-iron-cobalt-nickel eutectic high-entropy alloy created a herringbone-patterned microstructure that was extremely resistant to fracture (see the Perspective by An). The structure contained lamellae of hard and soft phases, and the cracks that formed in the hard phase were arrested at the boundary of the soft phase. This, along with stress transfer, allowed a tripling of the maximal elongation while retaining high strength. —BG

Precipitation-hardening high-entropy alloys (PH-HEAs) with good strength−ductility balances are a promising candidate for advanced structural applications. However, current HEAs emphasize near-equiatomic initial compositions, which limit the increase of intermetallic precipitates that are closely related to the alloy strength. Here we present a strategy to design ultrastrong HEAs with high-content nanoprecipitates by phase separation, which can generate a near-equiatomic matrix in situ while forming strengthening phases, producing a PH-HEA regardless of the initial atomic ratio. Accordingly, we develop a non-equiatomic alloy that utilizes spinodal decomposition to create a low-misfit coherent nanostructure combining a near-equiatomic disordered face-centered-cubic (FCC) matrix with high-content ductile Ni₃Al-type ordered nanoprecipitates. We find that this spinodal order–disorder nanostructure contributes to a strength increase of ~1.5 GPa (>560%) relative to the HEA without precipitation, achieving one of the highest tensile strength (1.9 GPa) among all bulk HEAs reported previously while retaining good ductility (>9%).