Metal–organic cages are processable porous molecules that can be assembled into a range of macroscopic porous materials.

NaYF ₄ and LiYF ₄ nanoparticles co-doped with Pr ³⁺ and Yb ³⁺ are reported, manifesting 980 nm excited downconversion luminescence peaked at 1320 nm for NIR-II bioimaging and 447 nm excited upconversion luminescence at 275 nm for germicide action.

Evolutionary selection in nature has led to hierarchical structuring as a fundamental optimization strategy for biological structures, maximizing functional performance while minimizing resource usage. Precise hierarchical organization of natural materials over a wide range of length scales gives rise to unique synergistic properties that could not be achieved by single components. Despite the clear advantages offered by hierarchically structuring matter, mastering hierarchical control based on the current synthetic toolbox is still a challenge. In this review, some recent advancements in the fabrication of hierarchical metal organic framework (MOF) materials are highlighted and the advantages that arise due to different kinds of MOF hierarchy are critically analyzed. The special focus of the review lies in highlighting the applications where MOF hierarchical materials can be most impactful and describing characterization techniques currently at the disposal of scientists for the precise characterization of MOF hierarchical structures across all length scales. Finally, the intent is to inspire reticular chemists to master hierarchical control of MOF materials so as to fully utilize the advantages MOFs offer for various applications.

The capability of materials to interconvert between different phases provides more possibilities for controlling materials’ properties without additional chemical modification. The study of state-changing microporous materials just emerged and mainly involves the liquefication or amorphization of solid adsorbents into liquid or glass phases by adding non-porous components or sacrificing their porosity. The material featuring reversible phases with maintained porosity is, however, still challenging. Here, we synthesize metal-organic polyhedra (MOPs) that interconvert between the liquid-glass-crystal phases. The modular synthetic approach is applied to integrate the core MOP cavity that provides permanent microporosity with tethered polymers that dictate the phase transition. We showcase the processability of this material by fabricating a gas separation membrane featuring tunable permeability and selectivity by switching the state. Compared to most conventional porous membranes, the liquid MOP membrane particularly shows the selectivity for CO₂ over H₂ with enhanced permeability.