The four first generations of dendrigraft poly-L-lysine have been studied in dimethylformamide (aprotic solvent) and in 0.2 M NaCl aqueous solutions by isothermal translation diffusion, ¹H NMR and viscometry methods. The relationships between diffusion coefficient, intrinsic viscosity and molar mass have been determined for dendrigraft poly-L-lysines, and the scaling index values have been compared to classical trifunctional dendrimers. Dendrimers and dendrigraft poly-L-lysines exhibited similitudes in their hydrodynamic behaviors. Nevertheless, dendrigraft poly-L-lysines displayed a specific behavior in solution. In contrast to dendrimers, a significant change of hydrodynamic dimension of dendrigraft poly-L-lysines according to the nature of the solvent has been observed. In aprotic solvent, the dendrigraft poly-L-lysine dimensions are about two times lower than in aqueous media (i.e., the hydrodynamic volume is contracted by a factor 8 in dimethylformamide), revealing the softness of dendrigraft poly-L-lysine compared to classical trifunctional dendrimers.

A homologous series of the chitosan derivative N-[(2-hydroxy-3-trimethylammonium)pro-pyl]chitosan in a 0.33 M CH3COOH + 0.2 M CH3COO Na mixture is studied via viscometry and static and dynamic light s

As shown by hydrodynamic, electrooptical, and computer-simulation studies, film-forming addition silicon-substituted polynorbornene and silicon-substituted poly(1-trimethylsilyl-1-propyne), which have

Seven polynorbornene samples containing trimethylsilyl side groups that were prepared by the addition polymerization of 5-trimethylsilyl-2-norbornene in the presence of catalytic systems (π-C₅H₉NiCl)₂-methylaluminoxane and nickel naphthenate-methylaluminoxane have been studied by translational isothermal diffusion and viscometry. The molecular masses of the polymer samples are measured. Kuhn-Mark-Houwink equations for diffusion coefficient D and intrinsic viscosity [η] are determined in toluene at 25°C: D = 6.94 × 10⁻⁴ M ^−0.61 and [η] = 1.53 × 10⁻³ M ^0.82. The equilibrium rigidity of polymers chains is estimated as A = 47 ± 9 Å. The conformational features of the silicon-containing polynorbornene are analyzed by the PM3 quantumchemical semiempirical method on the basis of simulation of its decamer chain fragments. In terms of microstructure and equilibrium rigidity, the above-described addition poly(trimethylsilylnorbornene) is close to poly(trimethylsilylpropyne) synthesized using niobium pentachloride as a catalyst. This finding explains similar membrane gas-separation properties of these polymers.