The development of Pt-based catalysts for use in fuel cells that meet performance targets of high activity, maximized stability, and low cost remains a huge challenge. Herein, we report a nitrogen (N)-doped high-entropy alloy (HEA) electrocatalyst that consists of a Pt-rich shell and a N-doped PtCoFeNiCu core on a carbon support (denoted as N-Pt/HEA/C). The N-Pt/HEA/C catalyst showed a high mass activity of 1.34 A mg_Pt^-1 at 0.9 V for the oxygen reduction reaction (ORR) in rotating disk electrode (RDE) testing, which substantially outperformed commercial Pt/C and most of the other binary/ternary Pt-based catalysts. The N-Pt/HEA/C catalyst also demonstrated excellent stability in both RDE and membrane electrode assembly (MEA) testing. Using operando X-ray absorption spectroscopy (XAS) measurements and theoretical calculations, we revealed that the enhanced ORR activity of N-Pt/HEA/C originated from the optimized adsorption energy of intermediates, resulting in the tailored electronic structure formed upon N-doping. Furthermore, we showed that the multiple metal-nitrogen bonds formed synergistically improved the corrosion resistance of the 3d transition metals and enhanced the ORR durability.

The biggest obstacle to the widespread implementation of polymer electrolyte membrane fuel cells (PEMFCs) is their cost, primarily due to the use of platinum catalysts. The high intrinsic catalyst activity exhibited on a rotating disk electrode (RDE) is rarely realized in a membrane electrode assembly (MEA), which is a long-standing challenge for PEMFCs and a cause of low catalyst utilization. To translate the high RDE performance of a catalyst into a MEA, the design of an ideal ionomer/catalyst interface is proposed: a thin, conformal ionomer film covers the maximum surface of a Pt nanoparticle and thus simultaneously maximizes catalyst utilization, (i.e., high mass activity and electrochemically active surface area) and O₂ diffusion rate (i.e., high current density performance) without compromising proton conduction. Building such an interface is a long-standing challenge due to the lack of interaction between the ionomer and catalyst particles, resulting in large ionomer agglomerates and inhomogeneous ionomer coverage over the catalyst nanoparticle, with consequent poor fuel cell performance. In this work, this ionomer/catalyst interface has been engineered, utilizing the electrostatic attraction between positively charged catalyst and negatively charged ionomer particles in a catalyst ink and preserved in a solid catalyst layer. As a result, this interface leads to previously unachieved proton exchange membrane fuel cell performance in terms of both catalyst utilization (75% vs. 45%) and peak/rated power density (i.e., 1.430/0.930 W cm⁻², H₂/air, cathode Pt loading: 0.1 mg_Pt cm⁻²) for pure Pt catalysts, even better than those of Pt alloy catalysts. This work demonstrates the formation of an interface in the liquid phase (using ultra-small-angle X-ray scattering in combination with cryo-TEM, isothermal–titration–calorimetry) and the preservation of the interface in the solid catalyst layer (using TEM) and estimates the effective coverage and thickness of the ionomer film (using limiting current density, RDE and fuel cell performance).

The strain effect of high-entropy intermetallic (HEI) catalysts on oxygen reduction reaction (ORR) performance remains largely unexplored, primarily due to the significant challenges associated with characterizing and calculating the intricate local coordination environments. Here, we design a nitrogen (N)-doped L1₀-ordered PtCoNiFeCu intermetallic catalyst supported on Ketjenblack carbon (N-HEI/KB), and reveal the origin of the sub-angstrom strain in N-HEI and its impact on ORR performance by combining atomic-scale characterization and theoretical calculations. The synergistic interplay of the sub-angstrom strain, the pinning effect of metal-N bonds, and the high-entropy effect contribute to the competitive stability of N-HEI/KB catalysts, providing high current density of 1388 mA cm^-2 at 0.7 V after 90,000 cycles even under harsh heavy-duty vehicle conditions. These findings broaden the avenues for designing high-performance high-entropy intermetallic cathode electrocatalysts.