The performance of a new dye-sensitized solar cell (DSSC) based in a natural dye extracted from the Bougainvillea spectabilis’ bracts, is reported. The performance of this solar cell was compared with cells prepared using extract of the Bougainvillea glabra and mixture of both extracts; in both cases the pigments were betalains, obtained from Reddish-purple extract. These dyes were purified to different extents and used for the construction of solar cells that were electrically characterized. The materials were characterized using FTIR and UV-Vis. Solar cells were assembled using TiO₂ thin film on indium tin oxide (ITO)-coated glass; a mesoporous film was sensitized with the Bougainvillea extracts. The obtained solar energy conversion efficiency was of 0.48% with a current density J_SC of 2.29 mA/cm² using an irradiation of 100 mW/cm² at 25 °C.

Dye-Sensitized Solar Cells (DSSCs), based on TiO₂ and assembled using a dye from Beta vulgaris extract (BVE) with Tetraethylorthosilicate (TEOS), are reported. The dye BVE/TEOS increased its UV resistance, rendering an increase in the cell lifetime; the performance of these solar cells was compared to those prepared with BVE without TEOS. The efficiency η for the solar energy conversion was, for BVE and BVE/TEOS, of 0.89% ± 0.006% and 0.68% ± 0.006% with a current density Jsc of 2.71 ± 0.003 mA/cm² and 2.08 ± 0.003 mA/cm², respectively, using in both cases an irradiation of 100 mW/cm² at 25 °C. The efficiency of the BVE solar cell dropped from 0.9 ± 0.006 to 0.85 ± 0.006 after 72 h of operation, whereas for the BVE/TEOS, the efficiency remained practically constant in the same period of time.

Disks of synthetic hydroxyapatite agglutinated with a synthetic polymer and hydrated in a moisture fog, were prepared. A well-defined piezoelectric signal of these samples was obtained when a relative small compression stress of 35MPa (corresponding a force of 450daN) was applied; piezoelectric signals of up to 12mV were obtained with this stress. Two different compression methods were followed to obtain the piezoelectric signal: (a) hold method, where the load was maintained constant once it reaches the maximum stress and (b) release method, where the load was removed rapidly when the stress reaches its maximum value. The samples were characterized using the techniques: X-ray Diffraction, Dielectric Relaxation Spectroscopy and mechanical test