ZnO nanorods were formed by chemical bath deposition on fluorine–doped tin oxide (FTO) glass and the photovoltaic performance of ZnO-based dye-sensitized solar cells (DSCs) was investigated. A DSC with 8 h-grown ZnO nanorods showed a higher power conversion efficiency (PCE) than devices with 4, 6, and 10 h-grown ones. Further improvement in PCE was achieved in a cell with a silver-ion-deposited ZnO/FTO electrode. By deposition of Ag⁺ on the surface of the 8 h-grown ZnO nanorods, the dye-loading amount increased by approximately 210%, compared to that of pristine ZnO nanorods, resulting in a 1.8-times higher PCE. A DSC with the pristine ZnO/FTO electrode showed a PCE of 0.629%, while in a device with the silver-ion-deposited ZnO/FTO, the PCE increased to 1.138%. In addition, interfacial resistance at the ZnO/dye/electrolyte was reduced to approximately 170 Ω from 460 Ω for the control cell with the pristine ZnO/FTO. We attributed the higher dye-loading amount in the silver-ion-deposited ZnO/FTO to the electrostatic attraction between the positively charged ZnO and carboxylate anions (–COO⁻) of the N719 dyes.

Highly porous carbon electrodes for supercapacitors with high energy storage performance were prepared by using a new precursor blend of aromatic polyimide (PI) and polyvinylidene fluoride (PVDF). Supercapacitor electrodes were prepared through the electrospinning and thermal treatment of the precursor blends of aromatic PI and PVDF. Microstructures of the carbonized PI/PVDF nanofibers were studied using Raman spectroscopy. Nitrogen adsorption/desorption measurements confirmed their high surface area and porosity, which is critical for supercapacitor performance. Energy storage performance was investigated and carbonized PI/PVDF showed a high specific capacitance of 283 F/g at 10 mV/s (37% higher than that of PI) and an energy density of 11.3 Wh/kg at 0.5 A/g (27% higher than that of PI) with high cycling stability.