Calcium hydroxide-based materials were the gold standard in vital pulp therapies for decades’ despite of several shortcomings. However, calcium silicates have been discussed as an alternative to overcome these drawbacks. It was aimed to investigate the in-vivo effectiveness of different calcium silicates based materials in pulp capping in this study. A parallel-design, randomized controlled trial with 213 patients who has deep dentin caries, vital pulps and without spontaneous pain or history of swelling was designed. 525 M teeth were randomized, blinded and allocated to one of the five groups for pulp capping treatment (n = 105). All teeth were followed up clinically and radiographically (after 1st, 6th, 12th and 36th months) by blinded investigators. The clinical and radiographic success, and the effect of the pulp exposure to the success rate analyzed with Wald chi-square and Z tests. Clinical and radiographic success of MTA+ (86.3%, 85.4%) and Biodentine (79.4%, 80.1%) were found the highest. Although results of Theracal LC group (72.1%, 73.6%) were better than Dycal group (69.4%, 70.2%), the difference was nonsignificant (p > 0.05). Only in light-cured groups, (TheraCal LC & LC Calcihyd) pulpal exposure size effected the success of the materials (p < 0.05). MTA+ and Biodentine resulted better scores, when compared with TheraCal LC in large pulpal exposures (p < 0.05). After 36-month follow-up, both MTA+ and Biodentine were found to be the appropriate material for direct pulp capping in permanent teeth. The filler ingredient of the Theracal-LC eases the usage of calcium silicates but decreases the success rate.

This study examines the properties of nanobased dental restorative materials with nanoindentation method in a precise, repeatable, and comparable way. Microhybrid and nanohybrid composites, conventional glass ionomer materials, and light cured nanoionomer materials were utilised for the study. Specimen discs (r=10 mm,h=2 mm) were prepared to test the hardness, modulus of elasticity, yield strength, and fracture toughness values for each sample in a nanoindentation device with an atomic force microscopy add-on (n=25). Comparative analyses were performed by one-way ANOVA and post hoc Tukey tests. The hardness and modulus of elasticity values of nanocomposite were higher (2.58 GPa and 32.86 GPa, resp.) than those of other dental materials. Although glass ionomer exhibited a hardness that was similar to a nanoionomer (0.81 versus 0.87 GPa), glass ionomer had the lowest fracture toughness value (Kc=0.83 MPa/mm^0.5). The mechanical properties of resin composites improve with additional nanoscale fillers, unlike the glass ionomer material.

Aim: The purpose of this study is to compare the efficiency of fluorescence-aided caries excavation (FACE) to remove carious dentin primary teeth with that of conventional methods. Methods and Materials: After caries excavation was carried out, dentin surfaces were conventionally inspected using visual tactile criteria and 415 cavities which were classified as caries-free, re-inspected with Face-Light and caries detector dye (CDD) methods. Orange-red fluorescing areas classified as carious dentin, as well as stained carious dentin. All the data were recorded according to localization of the caries and determination efficiency of the methods. X ² test was used to compare the mean values of both Face-Light and dye applications, while Wilcoxon test performed to evaluate the effectiveness for each diagnostic method. Results: A total of 273 patients with 415 Class II (OM/OD) cavities (1.65 ± 0.52 teeth per patient) with carious lesions in molar and premolar teeth, were examined. Out of 415 teeth, in 149 teeth (35.9%) no caries findings had been illustrated. While FACE detected remaining carious or partially removed areas in 237 teeth (57.2%), CDD stained only 29 teeth by itself (P < 0.05). Conclusion: In conclusion, FACE has a higher detectability compared to visual inspection and caries detector dye in diagnosis and removal of carious dentin.

The aim of this study was to investigate the marginal fit and bond strength characteristics of onlay restorations manufactured by three-dimensional printing (Varseo XS, Bego GmbH, Bremen, Germany) and CAD/CAM (CAMcube, Montreal, QC, Canada) systems. Class II onlay cavities on sixty mandibular molars were prepared in cavities and restored in three separate groups using different fabrication methods. Digital and conventional impressions were taken to design the restorations in the CAD system (DWOS, Straumann GmbH, Freiburg, Germany). To evaluate the marginal fit and void volumes, all specimens were scanned with microcomputed tomography. A microshear test was performed to compare the bond strength of the restorations to the tooth surface. The marginal fit values measured for the 3D-printed and CAD/CAM onlay restorations were found to be at clinically acceptable levels ( 0.05). According to the microshear test results, the CAD/CAM group had the highest bond strength values before (34.82 MPa) and after (26.87 MPa) thermal cycling (p < 0.05), while the 3D-printed and conventionally produced onlays had similar results (p < 0.05). 3D printing technology is a promising option for indirect restorations; however, the post-production phase is as crucial as the printing and cementation phases.

The aim is to evaluate the mechanical properties of the composite and ceramic based indirect restorative materials used in dental treatments with scanning nanoindentation test (NT). Finite element analysis (FEA) was applied to investigate the stress distribution. Four hybrid composite materials; Indirect resin composite (IRC), Resin nanoceramic (RNC), Polymer infiltrated ceramic (PIC) and Zirconia-reinforced lithium-di-silicate (ZRC) were divided into two subgroups for NT (n = 20) and fracture test (n = 40). Statistical analyses were performed with independent t-test, ANOVA and post-hoc Tukey tests (p ≤ 0.05). The highest hardness, elasticity and fracture toughness were observed in ZRC (p = 0.001). Frequency of vertical root fractures in RNC and IRC were statistically lower than ZRC (p = 0.032). Reinforced CAD-CAM ceramics revealed higher mechanical properties compared with IRC materials. The FEA model for fracture mechanism of RNC demonstrated lowest stress values and uniform stress distribution amongst all groups, while ZRC and PIC presented the highest fracture toughness.

Objective: The aim of this in-vitro study was to evaluate the efficacy of bleaching products, determine the applicability and validation of the measurement methods. Materials and Methods: Freshly extracted 110 human incisor teeth were stained with whole blood and hemolysate solution prior to the application of 10 different home-bleaching products. Spectrophotometric measurements of the tooth shades were performed for each specimen before and after bleaching at the 1^st, 3^rd, 7^th, and 14 days. Differences in lightness (Δl), chroma (Δc), hue (Δh) values and shade changes were measured to evaluate process. Computerized digital imaging analyses to determine the color changes were performed with Photoshop CS4 software (Adobe, San Jose, CA, USA). Statistical analyses were performed with analysis of variance, Scheffe and Tukey tests. Results: In all of the test groups regardless of the material used, a significant increase in lightness and hue, and decrease of chroma were observed, as compared to the control group. After recommended bleaching applications, Δl and Δh values respectively increased in group Zaris White and Brite (ZWB) and group Pola Night and Δc values showed significant decrease in groups ZWB and Rembrandt REM3 (P < 0.05). At the end of the procedure both spectrophotometric and digital imaging analysis showed ZWB was the most effective product among the others while Yotuel and Happy Smile were the least (P < 0.05). Conclusions: Home-bleaching systems showed slower but almost permanent bleaching effect likewise office-based methods. Both software and spectrophotometric analyses have advantages such as evaluating the results objectively and numerically, also treatment outcomes could be preserved.