This research investigated the relationship between volume energy density and the microstructure, density, and mechanical properties of the Ti-5Al-5Mo-3V-1Cr-1Fe alloy fabricated via the SLM process. The results indicate that an increase in volume energy density can promote a transition from a columnar to an equiaxed grain structure and suppress the anisotropy of mechanical properties. Specifically, at a volume energy density of 83.33 J/mm³, the average aspect ratio of β grains reached 0.77, accompanied by the formation of numerous nano-precipitated phases. Furthermore, the relative density of the alloy initially increased and then decreased as the volume energy density increased. At a volume energy density of 83.33 J/mm³, the relative density reached 99.6%. It is noteworthy that an increase in volume energy density increases the β grain size. Consequently, with a volume energy density of 83.33 J/mm³, the alloy exhibited an average grain size of 63.92 μm, demonstrating optimal performance with a yield strength of 1003.06 MPa and an elongation of 18.16%. This is mainly attributable to the fact that an increase in volume energy density enhances thermal convection within the molten pool, leading to alterations in molten pool morphology and a reduction in temperature gradients within the alloy. The reduction in temperature gradients promotes equiaxed grain transformation and grain refinement by increasing constitutive supercooling at the leading edge of the solid–liquid interface. The evolution of molten pool morphology mainly inhibits columnar grain growth and refines grain by changing the grain growth direction. This study provided a straightforward method for inhibiting anisotropy and enhancing mechanical properties.

This paper focuses on the fabrication of as-forged Ti46.5Al2Cr1.8Nb-(W, B) alloy via pulse current auxiliary isothermal forging (PCIF). The starting material composed of near gamma (NG) microstructure was fabricated by adopting pre-alloyed powders via hot pressing sintering (HPS) at 1300 °C. Isothermal compression tests were conducted at a strain rate range of 0.001–0.1 s⁻¹ and a temperature range of 1125–1275 °C to establish the constitutive model and processing map. The optimal hot deformation parameters were successfully determined (in a strain rate range of 10⁻³–2.5 × 10⁻³ s⁻¹ and temperature range of 1130–1180 °C) based on the hot processing map and microstructure observation. Accordingly, an as-forged TiAl based alloy without cracks was successfully fabricated by PCIF processing at 1175 °C with a nominal strain rate of 10⁻³ s⁻¹. Microstructure observation indicated that complete dynamic recrystallization (DRX) and phase transformation of γ→α₂ occurred during the PCIF process. The elongation of as-forged alloy was 136%, possessing a good secondary hot workability, while the sintered alloy was only 66% when tested at 900 °C with a strain rate of 2 × 10⁻⁴ s⁻¹.

A solid-state repair technique based on surface friction welding is investigated in depth to achieve excellent mechanical properties of damaged 7A52 aluminum alloy. The results show that the yield strength and tensile strength along the repair direction are 436 MPa and 502 MPa, respectively, at a rotational speed of 1400 rpm and a travel speed of 300 mm/min, which are about 157.9% and 129.7% of those before the defects were repaired, respectively, while the elongation is 17.2% compared to the base material. Perpendicular to the repair direction, the yield strength and tensile strength are 254 MPa and 432 MPa, which are 111.4% and 129.7% of those before the defects were repaired, respectively, while the elongation is 11.8% compared to the base material. The mechanical properties of the repaired areas are still improved compared to those of the defect-free sheets. On the one hand, this is attributed to the dynamic recrystallization of the nugget zone due to the thermo-mechanical coupling, resulting in the formation of a fine, equiaxed grain structure; on the other hand, the precipitated Mg₂Si phase, which is incoherent within the base material, transforms into the Al₁₂(Fe, Mn)₃Si phase, as well as the precipitation of the Al₆Mn phase and η′ phase, resulting in the enhancement of the properties. The material fracture at the junction of the nugget zone and the heat-affected zone occurs after repair, which is attributed to the significant difference in the texture of the nugget zone and the heat-affected zone, as well as to the stress concentration at the junction.