Microwave radiation is widely utilized in construction practice, especially for drying building materials, remediating damp masonry, or sterilization of biotic pests that have infested building structures. The available scientific and technical literature reports that certain materials exposed to microwave radiation do not change their physical and mechanical properties, although this has not yet been adequately verified. This paper builds on many years of research in the area, adding to and refining existing information, providing new insights into the mechanical and physical properties of commonly available building materials that have been exposed to controlled microwave radiation, and comparing them with reference values. The experimental research on a set of clay brick samples is carried out using tests according to European standards, and it focuses on the effect of microwave radiation on compressive strength and water absorption. The experimental samples were compared to reference samples that had not been subjected to prolonged exposure to moisture and were subsequently treated with microwave radiation for dehumidification.

The present paper deals with the properties of hardened cement mixtures that have been exposed to microwave radiation. Microwaves fall under electromagnetic waves (EMW), and the main reason for using EMW radiation is to accelerate the drying of concrete as well as to reduce the time required to obtain the handling strength after it is removed from the mould. This paper is divided into two main parts. In the first part, three sets of cement samples were made. One set of samples solidified naturally in air and the second and third sets of samples were exposed to EMW radiation, with different exposure times for each. The solidification was then stopped, and the representation of the major minerals was experimentally determined. The second part of the experiment focuses on the properties of the hardened cement mixtures, both in terms of strength and physical properties. The experiment was carried out on two sets of samples. Each mixture was exposed to EMW radiation, the main differences being the exposure time and the position of the samples relative to the EMW generator. The aim of the experiments is to determine the resulting mechanical properties of the samples in comparison with those that were subjected to normal solidification in air. The data from these experiments suggest that microwave radiation can be used to accelerate the curing of concrete specimens, obtaining the handling strength in a relatively short time, but a reduction in the resulting strength can be expected compared to the reference specimens.

This article raises awareness of Building Information Management (BIM) and its significance for Construction 4.0. BIM is often mistakenly understood only as a 3D model of a building object, but its true potential lies in the information associated with the model (e.g., mechanical and physical properties, costs, etc.). Models can subsequently be used in the building energy management (BEM) at all stages of the building object’s life cycle. This article focuses on the possibility of creating a model using available libraries in the Czech Republic provided by manufacturers and suppliers of building materials and the subsequent use of the model for energy modelling. The results obtained from computational modelling are then compared with real values measured on a timber construction located in Ostrava (Czech Republic). These results show that properly configured BIM modelling allows faster data processing while maintaining the quality of outputs and results. Additionally, there is potential to eliminate common pitfalls in the design and subsequent processing of thermal assessments of building objects.

The present work analyzes the effect of releasing physically bound water from hydrogel, cork, perlite, and ceramsite on materials exposed to microwave radiation and subsequently investigates possible changes in the physical properties of these materials (water absorption and thermal conductivity coefficient). The release of physically bound water from individual materials has potential practical applications in materials engineering, for example, in the internal curing of concrete, where individual aggregates could, under the influence of microwave radiation, release water into the structure of the concrete and thus further cure it. Experimental analysis was carried out with samples of the above-mentioned materials, which were first weighed and then immersed in water for 24 h. Then, they were weighed again and exposed to microwave radiation. After exposure, the samples were weighed again, left immersed in water for 24 h, and weighed again. The focus of the study was on the ability of the aggregates to release water due to microwave radiation and on the changes in the properties (water absorption, thermal conductivity coefficient) of these materials when exposed to microwave radiation. The samples were further monitored by digital microscopy for possible changes in the surface layer of the materials. The hydrogels show the highest water absorption (1000%) and the fastest water release (45 min to complete desiccation). After the release of water due to microwave radiation, their ability to absorb water is maintained. Of interest, however, is that in the case of almost complete removal of water from the soaked hydrogel, the original powdered state of the hydrogel is not obtained, but the outcome has rather a solid structure. In the case of cork, the water absorption depends on the fraction of the material.

An important part of building process is knowledge of thermal isolation materials and their exploitation. Because of higher demands of using thermal energy in buildings these materials are more important than ever. Main task of thermal isolation materials is creating inhibition of heat transfer. We want to create thermal isolation materials with convenient mechanical properties and low density, which is important for coefficient of thermal conductivity. There is many thermal isolation materials such as foam polystyrene, silicate isolation materials, vacuum isolation materials and new thermally reflective foils.