The wood processing industry produces a significant amount of wood waste. Biomass valorization through pyrolysis has the potential to increase the added value of wood wastes. Pyrolysis is an important thermochemical process that can produce solid, liquid, and gas products. This paper aims to review the pyrolysis of wood wastes from Indonesia, including teak wood (Tectona grandis), meranti (Shorea sp.), sengon (Paraserianthes falcataria (L) Nielsen), and rubberwood (Hevea brasiliensis). The review is based on an in-depth study of reliable literatures, statistical data from government agencies, and direct field observations. The results showed that pyrolysis could be a suitable process to increase the added value of wood waste. Currently, slow pyrolysis is the most feasible for Indonesia, with the main product of charcoal. The efficiency of the slow pyrolysis process can be increased by harvesting also liquid and gaseous products. The use of the main product of pyrolysis in the form of charcoal needs to be developed and diversified. Charcoal is not only used for fuel purposes but also as a potential soil improvement agent.

The present study investigates the quality changes of wood bio-briquette fuel after the addition of spent coffee ground (SCG) into the initial feedstock materials (sawdust, shavings) in different mass ratios (1:1, 1:3). Analysis of SCGs fuel parameter proved great potential for energy generation by a process of direct combustion. Namely, level of calorific value (GCV = 21.58 MJ∙kg⁻¹), of ash content (Ac = 1.49%) and elementary composition (C = 55.49%, H = 7.07%, N = 2.38%, O = 33.41%) supports such statement. A comparison with results of initial feedstock materials exhibited better results of SCG in case of its calorific value and elementary composition. Bulk density ρ (kg·m⁻³) and mechanical durability DU (%) of bio-briquette samples from initial feedstock materials were following for sawdust: ρ = 1026.39 kg·m⁻³, DU = 98.44% and shavings: ρ = 1036.53 kg·m⁻³, DU = 96.70%. The level of such mechanical quality indicators changed after the addition of SCG. Specifically, SCG+sawdust mixtures achieved ρ = 1077.49 kg·m⁻³ and DU = 90.09%, while SCG + shavings mixtures achieved ρ = 899.44 kg·m⁻³ and DU = 46.50%. The addition of SCG increased wood bio-briquettes energy potential but decreased its mechanical quality. Consequently, the addition of SCG in wood bio-briquette has advantages, but its mass ratio plays an important key role.

Sugarcane bagasse, the solid waste material produced in the sugar industry, was subjected to treatment in hot compressed water. The experiments were performed in a batch-type reactor containing slurry of 10 ml of water and 1.2 g of solids. The reactor was heated to temperatures ranging between 200°C and 300°C for reaction times of 3 to 30 min. The product was separated into liquid and solid fractions. Each fraction was analyzed to investigate the alteration of the main lignocellulosic polymers by hot compressed water. Results for the liquid fractions showed that increased temperatures and reaction times completely dissolved hemicellulose and cellulose in the water, leaving lignin in the solid product. During treatment, hemicellulose and cellulose gradually decomposed into simple sugars, which were then degraded and decomposed into furfural, 5-(hydroxymethyl)furfural (5-HMF) and organic acids. However, the yield of furans and some organic acids decreased and became undetectable at 300°C and with increasing reaction time. The solid fraction was also characterized before and after treatment. Results showed that the hydrogen and oxygen content of the solids decreased with increased reaction conditions, due to dehydration and decarboxylation reactions. The reactions also increased the carbon content of the treatment products by 1.2–1.6 times that in the raw material, suggesting that the hot compressed water treatment of sugarcane bagasse can be considered for the provision of valuable chemicals for biofuel and high-carbon-content material (biochar).