Pressure ulcers are difficult to treat. Recent reports of low-temperature atmospheric-pressure plasma (LTAPP) indicated its safe and effectiveness in chronic wound care management. It has been shown both in vitro and vivo studies that LTAPP not only helps facilitate wound healing but also has antimicrobial efficacy due to its composition of ion and electron, free radicals, and ultraviolet ray. We studied the beneficial effect of LTAPP specifically on pressure ulcers. In a prospective randomized study, 50 patients with pressure ulcers were divided into 2 groups: Control group received standard wound care and the study group was treated with LTAPP once every week for 8 consecutive weeks in addition to standard wound care. We found that the group treated with LTAPP had significantly better PUSH (Pressure Ulcer Scale for Healing) scores and exudate amount after 1 week of treatment. There was also a reduction in bacterial load after 1 treatment regardless of the species of bacteria identified.

The aim of this study was to evaluate the effects of plasma treatment on adhesion between fiber-reinforced posts and a composite core material. Two types of posts, methacrylate-based (FRC Postec) and epoxy resin-based (DT Light-Post), were treated with oxygen plasma (O2), argon plasma (Ar), nitrogen plasma (N2), or helium mixed with nitrogen plasma (He+N2) using a radio-frequency generator before bonding to a methacrylate-based composite. Pull-out tests were performed using a universal testing machine. Surface roughness of each group was evaluated using a profilometer. On tensile-shear bond strength, statistical analysis revealed that the type of post, type of plasma treatment, and their interaction significantly influenced the results (p<0.05). Tukey’s test revealed significant differences in tensile-shear bond strength between the control and other plasma treatment groups (p<0.05). On surface roughness, Tukey’s test revealed significant differences between the control group and the Ar group (p<0.05) with DT Light Post. Plasma treatment appeared to increase the tensile-shear bond strength between post and composite.