The construction of heavy polar icebreakers is usually done with special hull steels, which require comprehensive properties such as good low-temperature toughness, high strength, and superior fatigue resistance. Reasonable and satisfactory heat treatments should be investigated and applied to acquire the required high strength and superior low-temperature toughness, since this is deemed an effective approach to ameliorate the combined properties of high-strength hull steels. Regarding this, the present study specifically explores the effects of different laboratory-based quenching (850 to 930 °C) and tempering (580 to 660 °C) heat treatments on the final low-temperature toughness of the high-strength hull steels. The low-temperature toughness is eventually improved without significantly sacrificing the strength. The results show that a favourable combination of properties can be obtained in the specimens under 900 °C quenching and 660 °C tempering processes. Additionality, the specimens tempered at 620 °C present the highest hardness, owing to the higher percentage of tempered martensite. Detailed mechanisms of the enhanced properties of the typical specimens subjected to the corresponding quenching and tempering processing are analysed and explicated.

Retained austenite (RA) transformation and its role in the mechanical properties of three low-carbon micro-alloyed quenching and partitioning (Q&P) steels was investigated utilizing in situ tensile tests and electron microscopy. Meanwhile, RA’s strain-induced martensite transformation (SIMT) was analyzed and discussed in terms of the strengthening mechanism. The results show that the ductility of the Q&P steels relies on the size and morphology of RA. In addition, both affect RA’s mechanical or thermostability. Dislocation density and carbon trapping should be considered in estimating the yield strength in the two-step Q&P process. V and Nb-Ti elements promote the formation of blocky RA. Ti accelerates the formation of film-like RA. For experimental Q&P steels with different processes and compositions, the true stress always keeps a linear relationship with the amount of transformed martensite, i.e., 30.38~46.37 MPa per vol. 1% transformed martensite, during the in situ tensile deformation.

In order to obtain the good match between yield strength and low-temperature toughness, the short-time partial austenitization (SPA) process was employed for V-microalloying 0.22C-5.24Mn steel. The initial microstructure after intercritical tempering was dual-phase ferrite and reversed austenite (RA), while the final microstructure was consisted of ferrite, RA and secondary martensite (SM) after subjected to SPA process. (V, Mo)C with disc-like morphology mainly precipitated during intercritial tempering, and the aspect ratio of particle decreased, leading to the appearance of near-spherical morphology. After subjected to SPA process, the resultant multiphase hierarchical microstructure (three layers: out layer of ferrite, interlayer of SM and inner layer RA) enabled high yield strength of 1097 MPa, total elongation of 14%, and impressive impact energy of 33.3 J at -20 °C. The strengthening contribution of (V, Mo)C precipitation was estimated about 108 MPa.

In order to obtain the good match between yield strength and low-temperature toughness, the short-time partial austenitization (SPA) process was employed for V/Mo-bearing 0.22C–5.24Mn steel. The initial microstructure after intercritical tempering was dual-phase ferrite and reversed austenite (RA), while the final microstructure consisted of ferrite, RA, and secondary martensite (SM) after being subjected to the SPA process. (V, Mo)C with disclike morphology mainly precipitated during intercritical tempering, and the aspect ratio of particles decreased, leading to the appearance of near-spherical morphology. After being subjected to SPA process, the resultant multiphase hierarchical microstructure (three layers: outer layer of ferrite, interlayer of SM, and inner layer of RA) enabled a high yield strength of 1097 MPa, a total elongation of 14%, and an impressive impact energy of 33.3 J at −20 °C. The strengthening contribution of (V, Mo)C precipitation was estimated to be about 108 MPa.