This study evaluated color stability, surface roughness and flexural strength of acrylic resin specimens after immersion in alkaline peroxide and alkaline hypochlorite, simulating a period of one and a half year of use of overnight immersion. Sixty disc-shaped (16X4 mm) and 80 rectangular specimens (65X10X3.3 mm) were prepared from heat-polymerized acrylic resin (Lucitone 550) and distributed into 4 groups (n=20): C1: without immersion, C2: 8 h immersion in distilled water; AP: 8 h immersion in alkaline peroxide effervescent tablet; SH: 8 h immersion in 0.5% NaOCl solution. Properties were evaluated at baseline and after the immersion. Color data were also calculated according the National Bureau of Standards (NBS). Results were analyzed statistically by ANOVA and Tukey's HSD test (α=0.05). AP (2.34 ± 0.41) caused color alteration significantly higher than C2 (0.39 ± 0.30) and SH (1.73 ± 0.52). The mean ΔE values were classified as indicial for C2 (0.36 ± 0.29) and noticeable for AP (2.12 ± 0.39) and SH (1.59 ± 0.48). SH (0.0195 ± 0.0150) caused significantly higher ΔRa (p=0.000) than the C2 (0.0005 ± 0.0115) and PA (0.0005 ± 0.0157) groups. There was no statistically significant difference (p=0.063) among the solutions for flexural strength (C1: 105.43 ± 14.93, C2: 100.30 ± 12.43, PA: 97.61 ± 11.09, SH: 95.23 ± 10.18). In conclusion, overnight immersion in denture cleansing solutions simulating a year and a half of use did not alter the flexural strength of acrylic resin but caused noticeable color alterations, higher for alkaline peroxide. The 0.5% NaOCl solution caused increase in surface roughness.

To preserve oral health and to maintain the prosthetic devices, it is important not only to improve the properties of commonly known hygiene products, but also to investigate new materials with antimicrobial action.

The objective of this in vitro study was to investigate the effect of nanostructured silver vanadate decorated with silver nanoparticles (AgVO₃) on antimicrobial activity, hardness, roughness, and adhesion of a soft denture liner. The antimicrobial efficacy of the Trusoft (Boswoth) liner incorporated with different concentrations of AgVO₃ against Enterococcus faecalis, Pseudomonas aeruginosa, Candida albicans, and Staphyloccocus aureus (n = 5) was evaluated by the agar diffusion method. Roughness, hardness, and adhesion properties were also evaluated. The data were analyzed by analysis of variance (ANOVA) and Tukey’s multiple comparison test with significance at the p < 0.05 level. At concentrations of 1 and 2.5%, AgVO₃ incorporation was effective only against E. faecalis, and at 5 and 10%, against E. faecalis, P. aeruginosa, and C. albicans. None of the concentrations was effective against S. aureus. A decrease in hardness was found for the 1, 2.5, and 10% AgVO₃ concentrations (p < 0.001) and at 5%, hardness was not affected. None of the concentrations affected the roughness of the material. A significant increase in tensile values was observed between the liner and heat-curing acrylic resin for 2.5% (p < 0.001) and 10% (p = 0.042) concentrations. AgVO₃ incorporation to a soft denture liner promoted antimicrobial activity against E. faecalis, P. aeruginosa, and C. albicans without affecting roughness, maintaining the hardness properties recommended for soft and extra soft liners, and improving the adhesion between the liner and the acrylic resin used for dentures.