Developments in polymer 3D printing (3DP) technologies have expanded their scope beyond the rapid prototyping space into other high-value markets, including the consumer sector. Processes such as fused filament fabrication (FFF) are capable of quickly producing complex, low-cost components using a wide variety of material types, such as polylactic acid (PLA). However, FFF has seen limited scalability in functional part production partly due to the difficulty of process optimization with its complex parameter space, including material type, filament characteristics, printer conditions, and “slicer” software settings. Therefore, the aim of this study is to establish a multi-step process optimization methodology—from printer calibration to “slicer” setting adjustments to post-processing—to make FFF more accessible across material types, using PLA as a case study. The results showed filament-specific deviations in optimal print conditions, where part dimensions and tensile properties varied depending on the combination of nozzle temperature, print bed conditions, infill settings, and annealing condition. By implementing the filament-specific optimization framework established in this study beyond the scope of PLA, more efficient processing of new materials will be possible for enhanced applicability of FFF in the 3DP field.

Metal powder-based additive manufacturing (AM) relies on consistently successful processing of feedstock powder, necessitating through-process predictability in powder properties and behavior. However, routine powder handling and storage may degrade powder performance by influencing flowability and moisture content through exposure to ambient conditions. Therefore, this study aimed to evaluate the effects of repeated environmental exposure on the flowability and moisture content of Al 5056 and Ta powders for AM applications. Using Carney Funnel flow tests, thermogravimetric analysis, and particle size/shape analysis, powder characterization helped elucidate powder property and behavioral changes with exposure. Results indicated inconsistent flowability and moisture content changes for both material types when exposure conditions were altered. Correlational statistics highlighted the most influential particle characteristics on powder behavior after exposure; particle morphology was most impactful for the semi-spherical Al 5056, whereas moisture content and particle size were most significant for the angular Ta. While exposure to laboratory conditions minimally changed powder performance in this study, caution is advised when handling and storing powders in more “extreme” environments. Powder users are urged to implement quality controls alongside powder characterization to pinpoint how specific powders should be treated, handled, and stored in a given environment for successful processing in AM.

This work explores the impact of thermally preprocessing recycled austenitic stainless-steel powder for solid-state cold spray metal additive manufacturing with a focus on increasing deposition quality and coating density while maintaining mechanical integrity. The recycled stainless-steel scrap was gas-atomized using a novel mobile foundry manufactured by MolyWorks Materials Corporation. The powder was thermally treated based upon thermodynamic modeling using Thermo-Calc. The powder and sprayed specimens were characterized using particle size–shape analysis, microscopy, x-ray diffraction, and nanoindentation. Diffraction results highlighted the presence of both austenite and ferrite phases in the powder. Nanoindentation confirmed that thermally processing the feedstock powder at the austenitization temperature decreased the amount of ferrite present, which was consistent with the porosity observed in the deposits due to the lower yield strength of austenite relative to ferrite. The untreated powder deposits exhibited extensive porosity and microcracking, as opposed to the virtually fully dense deposit from the heat-treated powder.

The surface roughness of additively manufactured (AM) components can have deleterious effects on the properties of the final part, such as corrosion resistance and fatigue life. Modification of the surface finish or parts produced by AM processes, such as cold spray, through methods such as mass finishing, can help to mitigate some of these issues. In this work, the surface evolution of as-produced copper cold sprayed material consolidations was studied through mass finishing. Three different copper powders attained by different production methods and of different sizes were used as feedstock. The surface topography of the cold spray deposits was measured as a function of the mass finishing time for the three copper cold spray samples and analyzed in terms of relative area and complexity, revealing an inverse correlation relating material removal rate and hardness/strength of the cold sprayed deposits. The material removal rate was also affected by the quality of the cold spray deposition, as defined by deposition efficiency (DE). Large initial drops in relative area and complexity are also likely due to the removal of loosely bonded powders at the start of mass finishing. Based on this study, the cold spray parameters that affect the rate of mass finishing have been explored.