Lewis base molecules that bind undercoordinated lead atoms at interfaces and grain boundaries (GBs) are known to enhance the durability of metal halide perovskite solar cells (PSCs). Using density functional theory calculations, we found that phosphine-containing molecules have the strongest binding energy among members of a library of Lewis base molecules studied herein. Experimentally, we found that the best inverted PSC treated with 1,3-bis(diphenylphosphino)propane (DPPP), a diphosphine Lewis base that passivates, binds, and bridges interfaces and GBs, retained a power conversion efficiency (PCE) slightly higher than its initial PCE of ~23% after continuous operation under simulated AM1.5 illumination at the maximum power point and at ~40°C for >3500 hours. DPPP-treated devices showed a similar increase in PCE after being kept under open-circuit conditions at 85°C for >1500 hours.

A new nanocrystalline sensitizer with the chemical formula (CH₃CH₂NH₃)PbI₃ is synthesized by reacting ethylammonium iodide with lead iodide, and its crystal structure and photovoltaic property are investigated. X-ray diffraction analysis confirms orthorhombic crystal phase with a = 8.7419(2) Å, b = 8.14745(10) Å, and c = 30.3096(6) Å, which can be described as 2 H perovskite structure. Ultraviolet photoelectron spectroscopy and UV-visible spectroscopy determine the valence band position at 5.6 eV versus vacuum and the optical bandgap of ca. 2.2 eV. A spin coating of the CH₃CH₂NH₃I and PbI₂ mixed solution on a TiO₂ film yields ca. 1.8-nm-diameter (CH₃CH₂NH₃)PbI₃ dots on the TiO₂ surface. The (CH₃CH₂NH₃)PbI₃-sensitized solar cell with iodide-based redox electrolyte demonstrates the conversion efficiency of 2.4% under AM 1.5 G one sun (100 mW/cm²) illumination.

A facile and low-temperature process to prepare planar perovskite solar cells (PSCs) has led to considerable progress in flexible solar cells toward high throughput production based on a roll-to-roll process. However, the performance of planar PSCs is still lower than that of mesoscopic PSCs using a high temperature process. Here, we report a new concept of a low temperature processed porous planar electron transport layer (ETL) inspired by a mesoporous structure for improving the performance of flexible devices. The structurally and energetically designed porous planar ETL induced the formation of a high quality perovskite and a preferred band alignment, resulting in improved charge collection efficiency in a fabricated device. Through the porous planar ETL, we achieved a power conversion efficiency (PCE) of 20.7% with a certified efficiency of 19.9% on a flexible substrate, which is the highest PCE reported to date. In addition, for the first time, we succeed in fabricating a large area flexible module with the porous planar ETL, demonstrating a PCE of 15.5%, 12.9% and 11.8% on an aperture area of 100 cm², 225 cm² and 400 cm², respectively. We believe that this strategy will pave a new way for realizing highly efficient flexible PSCs.

Significance: Utilizing low-cost materials, sodium ion batteries (SIBs) are beginning to attract considerable attention, particularly for large-scale utility grid applications. However, electrochemical performance of most SIB active materials is still insufficient for various practical applications. In the current study, we discovered a vanadium-based ortho-diphosphate, Na ₇ V ₄ (P ₂ O ₇ ) ₄ PO ₄ , or VODP, that holds exceptional electrochemical properties represented by well-defined high voltage profiles at 3.88 V (vs. Na/Na ⁺ ) and substantial capacity retention over 1,000 cycles. A theoretical analysis suggests that an intermediate phase encountered during phase transformation of VODP is crucial for better kinetics during battery operations, which can be expanded as a general principle in understanding diverse battery materials.