Over the past three decades, researchers have investigated the existence of possible relationships between crystal nucleation kinetics and the atomic-scale structure of silicate glasses. The main driving force for this quest was the fact that while the vast majority of glass-forming substances only undergo surface (heterogeneous) nucleation when sufficiently heated, a few systems also show the thermodynamically less favourable case of internal (homogeneous) nucleation on laboratory time/length scales. For such glass systems, various macroscopic properties, such as densities, configurational entropies and frozen-in birefringence, have suggested that the structure in the glassy state shows a closer resemblance to the structure of the phase formed upon crystallisation than in the case of glass systems only undergoing heterogeneous nucleation. However, the specific structural features and their length scales have remained uncertain. In this article, we review and discuss the research investigating relationships between the occurrence of internal nucleation and structural parameters related to various different length scales. The latter include (1) short-range order, concerning both network modifier cation-oxygen distances and coordination numbers as well as network former Q ⁿ distributions, (2) intermediate range order describing network former connectivities, network former/network modifier correlations, and network modifier distance distributions, and (3) medium range order as reflected by silicate tetrahedral ring-size statistics. Inspection of this data for several stoichiometric oxide glasses and their respective isochemical crystals suggests a positive correlation between homogeneous nucleation ability and structural similarity at the level of short- and intermediate-range order of the network modifier cations. In contrast, no correlation can be found with regard to any structural parameters describing the local structures of the network former species ( Q ⁿ distributions). Based on the limited set of data available, we develop concrete recommendations for future experiments to test this hypothesis.

In this work, mixed alkali metaphosphate glasses based on K–Na, Rb–Na, Rb–Li, Cs–Na and Cs–Li combinations were studied by differential scanning calorimetry (DSC), complex impedance spectroscopy, and Raman spectroscopy. DSC analyses show that both the glass transition (T_g) and melting temperatures (T_m) exhibit a clear mixed-ion effect. The ionic conductivity shows a strong mixed-ion effect and decreases by more than six orders of magnitude at room temperature for Rb–Na or Cs–Li alkali pairs. This study confirms that the mixed-ion effect may be explained as a natural consequence of random ion mixing because ion transport is favoured between well-matched energy sites and is impeded due to the structural mismatch between neighbouring sites for dissimilar ions.

Enzymatic hydrolysis is a crucial step of biomass conversion into biofuels and different pretreatments have been proposed to improve the process efficiency. Amongst the various factors affecting hydrolysis yields of biomass samples, porosity and water accessibility stand out due to their intimate relation with enzymes accessibility to the cellulose and hemicellulose fractions of the biomass. In this work, sugarcane bagasse was subjected to acid and alkali pretreatments. The changes in the total surface area, hydrophilicity, porosity and water accessibility of cellulose were investigated by scanning electron microscopy (SEM) and nuclear magnetic resonance (NMR). Changes in chemical and physical properties of the samples, caused by the partial removal of hemicellulose and lignin, led to the increase in porosity of the cell walls and unwinding of the cellulose bundles, as observed by SEM. 1H NMR relaxation data revealed the existence of water molecules occupying the cores of wide and narrow vessels as well as the cell wall internal structure. Upon drying, the water molecules associated with the structure of the cell wall did not undergo significant dynamical and partial moisture changes, while those located in the cores of wide and narrow vessels kept continuously evaporating until reaching approximately 20% of relative humidity. This indicates that water is first removed from the cores of lumens and, in the dry sample, the only remaining water molecules are those bound to the cell walls. The stronger interaction of water with pretreated bagasse is consistent with better enzymes accessibility to cellulose and higher efficiency of the enzymatic hydrolysis. We were able to identify that sugarcane bagasse modification under acid and basic pretreatments change the water accessibility to different sites of the sample, associated with both bagasse structure (lumens and cell walls) and hydrophilicity (lignin removal). Furthermore, we show that the substrates with increased water accessibility correspond to those with higher hydrolysis yields and that there is a correlation between experimentally NMR-measured transverse relaxation times and the efficiency of enzymatic hydrolysis. This might allow for semiquantitative estimates of the enzymatic hydrolysis efficiency of biomass samples using inexpensive and non-destructive low-field 1H NMR relaxometry methods.