The use of pillared interlayered clays (PILCs) as heterogenous catalysts in wastewater treatment technologies, particularly advanced oxidation processes (AOPs), is gaining popularity for the treatment of refractory wastewater effluents.

Titanium dioxide (TiO2) has been widely used as a photocatalyst in many environmental and energy applications due to its efficient photoactivity, high stability, low cost, and safety to the environment and humans. However, its large band gap energy, ca. 3.2 eV limits its absorption of solar radiation to the UV light range which accounts for only about 5% of the solar spectrum. Furthermore, the photocatalytic activity of TiO2 is also limited by the rapid recombination of the photogenerated electron-hole pairs. When used in water treatment applications, TiO2 has a poor affinity toward organic pollutants, especially hydrophobic organic pollutants. Several strategies have been employed to reduce its band gap energy, its electron-hole recombination rates as well as enhance its absorption of organic pollutants. In this chapter, we review some of the most recent works that have employed the doping, decoration, and structural modification of TiO2 particles for applications in photocatalysis. Additionally, we discuss the effectiveness of these dopants and/or modifiers in enhancing TiO2 photoactivity as well as some perspective on the future of TiO2 photocatalysis.

Gold deposition on Hombikat UV100 was found to negatively affect the activity of this Anatase catalyst in selective photo-oxidation of cyclohexane. By ammonia TPD and DRIFT spectroscopy it was determined that the Au deposition procedure leads to a significant decrease in OH-group density (mol m⁻² _BET) on Hombikat, suggesting that the amount of surface OH-groups, rather than the presence or absence of Au, is determining the catalytic performance. The importance of surface OH-groups was demonstrated by comparing the performance of Hombikat (with and without Au deposition) to surface propoxylated TiO₂, synthesized by a sol–gel method from titanium (IV) isopropoxide. The effect of the deposition recipe of noble metals on the surface composition of TiO₂ should thus be taken into account in evaluating and explaining photocatalytic performance of TiO₂ modified by noble metals (Au), in particular in non-aqueous phase reactions.

The activity of gold/titania catalysts for the room-temperature oxidation of CO can be dramatically enhanced by the addition of sulfate ions to the support; it appears that anion promotion of gold may be a general phenomenon and may be related to the direct modification of active gold sites in the case of sulfate ions, as evidenced by secondary ion mass spectrometry.