In this study, the effects of titanium dioxide (TiO₂) nanoparticles on the sulfate attack resistance of ordinary Portland cement (OPC) and slag-blended mortars were investigated. OPC and slag-blended mortars (OPC:Slag = 50:50) were made with water to binder ratio of 0.4 and a binder to sand ratio of 1:3. TiO₂ was added as an admixture as 0%, 3%, 6%, 9% and 12% of the binder weight. Mortar specimens were exposed to an accelerated sulfate attack environment. Expansion, changes in mass and surface microhardness were measured. Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), X-ray Diffraction (XRD), Thermogravimetry Analysis (TGA) and Differential Scanning Calorimetry (DSC) tests were conducted. The formation of ettringite and gypsum crystals after the sulfate attack were detected. Both these products had caused crystallization pressure in the microstructure of mortars and deteriorated the mortars. Our results show that the addition of nano-TiO₂ accelerated expansion, variation in mass, loss of surface microhardness and widened cracks in OPC and slag-blended mortars. Nano-TiO₂ containing slag-blended mortars were more resistant to sulfate attack than nano-TiO₂ containing OPC mortars. Because nano-TiO₂ reduced the size of coarse pores, so it increased crystallization pressure due to the formation of ettringite and gypsum thus led to more damage under sulfate attack.

Various self-healing methods for concrete, such as the use of supplementary cementitious materials, adhesive agents, mineral admixtures, and bacteria, have been suggested to date, and each of these has merits and demerits. Among these, however, the use of cementitious materials may be appropriate due to their good healing efficiency, low cost, and compatibility with the cement matrix. In this study, granulation and coating methods were applied to a new cementitious composite material. The self-healing property of these materials was controlled by the polyvinyl alcohol (PVA) coating until cracks were created. Water dissolved the PVA coating after entering through the cracks, and reacted with the healing materials to generate healing products. The self-healing performance was evaluated at various elapsed times through the measurement of the crack widths, visual observation, and examination of the microscopic images. Simultaneously, a water permeability test was performed and the dynamic modulus of elasticity was measured to verify the recovery of the cracks. In addition, the healing products that had been formed in the cracks were analyzed via X-ray diffraction (XRD) and scanning electron microscopy (SEM).

This study investigates the potential of light-burnt dolomite (LBD) as a supplementary cementitious material with ground granulated blast furnace slag (GGBFS) and Ordinary Portland cement (OPC). In this work, LBD was substituted for up to 20% of GGBFS in sodium sulfate-activated slag systems. The effects of LBD incorporation on the flow, setting time, compressive and flexural strength development, and drying shrinkage were explored with, X-ray diffraction and thermogravimetric analyses. LBD incorporation resulted in greater strength development of an alkali-activated slag system. The optimum LBD content for strength development was 10%, regardless of ordinary Portland cement content. In addition, LBD decreased the drying shrinkage, accelerated the hydration process, and induced hydrotalcite formation, which can be attributed to the reactive MgO inside LBD.

The depletion of natural sand and production of the huge amount of cement in the construction industry are serious threats to the environment, which can be reduced by the utilization of by-products as cement replacement material. In this study, cement was replaced with fly ash up to 45% (by weight). In addition, the natural fine aggregate was replaced with air-cooled blast furnace slag aggregate (here referred to as “slag aggregate”) at a level of 50% and 100% (by weight). Polypropylene fiber was also added, at a dosage of 0.25% of binder weight. Mortar specimens were prepared and analyzed using tests for compressive, flexure, and splitting tensile strength, as well as for microhardness, and ultrasonic pulse velocity. In addition, the specimens were exposed to sulfate solution and investigated for changes in length, mass, and compressive strength. Electron microscopy and X-ray diffraction analysis were performed to examine the microstructure and phase changes of mortar specimens exposed to sulfate solution. The results indicate that mortar specimens made with 50% slag aggregate and 0.25 % fiber showed enhanced mechanical properties. The performance of slag aggregate mortars under sulfate attack was improved significantly.