Rehabilitation and mobility assistance using robotic orthosis or exoskeletons have shown potential in aiding those with musculoskeletal disorders. Artificial muscles are the main component used to drive robotics and bio-assistive devices. However, current fabrication methods to produce artificial muscles are technically challenging and laborious for medical staff at clinics and hospitals. This study aims to investigate a printhead system for material extrusion of helical polymer artificial muscles. In the proposed system, an internal fluted mandrel within the printhead and a temperature control module were used simultaneously to solidify and stereotype polymer filaments prior to extrusion from the printhead with a helical shape. Numerical simulation was applied to determine the optimal printhead design, as well as analyze the coupling effects and sensitivity of the printhead geometries on artificial muscle fabrication. Based on the simulation analysis, the printhead system was designed, fabricated, and operated to extrude helical filaments using polylactic acid. The diameter, thickness, and pitch of the extruded filaments were compared to the corresponding geometries of the mandrel to validate the fabrication accuracy. Finally, a printed filament was programmed and actuated to test its functionality as a helical artificial muscle. The proposed printhead system not only allows for the stationary extrusion of helical artificial muscles but is also compatible with commercial 3D printers to freeform print helical artificial muscle groups in the future.

Smart hinges fabricated using three-dimensional (3D) printing have been accepted in the aerospace, robotics, and biomedical fields since these devices possess a shape memory characteristic. Shape memory polymers (SMPs) are the preferred materials for creating smart hinges due to their ability to achieve programmable complex geometries. However, fabricating SMPs with embedded components remains a challenge due to the constraints of current 3D printing methods and material limitations. This study investigated the use of a hybrid 3D printing method, direct ink writing (DIW), and embedded 3D printing (e-3DP) to print smart hinges with an embedded circuit to act as a strain sensor. The main components of the SMP included tert-Butyl acrylate (tBA) and aliphatic urethane diacrylate (AUD), but this SMP ink had a low viscosity and could not be used for DIW or e-3DP. Fumed silica (FS) was added to the SMP to tune its rheology, and it was shown that the FS concentration significantly affected the rheological properties, dry-out process, filament geometries, and self-supporting capabilities. This study presents a hybrid 3D printing approach for creating smart hinges with internal strain sensors in one step, demonstrating the versatility of DIW/e-3DP. The findings from this work provide a foundational and reliable technical solution to efficiently fabricate functional, self-monitoring, smart devices from SMPs for diverse applications.

Astronauts suffer skeletal muscle atrophy in microgravity and/or zero-gravity environments. Artificial muscle-actuated exoskeletons can aid astronauts in physically strenuous situations to mitigate risk during spaceflight missions. Current artificial muscle fabrication methods are technically challenging to be performed during spaceflight. The objective of this research is to unveil the effects of critical operating conditions on artificial muscle formation and geometry in a newly developed helical fiber extrusion method. It is found that the fiber outer diameter decreases and pitch increases when the printhead temperature increases, inlet pressure increases, or cooling fan speed decreases. Similarly, fiber thickness increases when the cooling fan speed decreases or printhead temperature increases. Extrusion conditions also affect surface morphology and mechanical properties. Particularly, extrusion conditions leading to an increased polymer temperature during extrusion can result in lower surface roughness and increased tensile strength and elastic modulus. The shape memory properties of an extruded fiber are demonstrated in this study to validate the ability of the fiber from shape memory polymer to act as an artificial muscle. The effects of the operating conditions are summarized into a phase diagram for selecting suitable parameters for fabricating helical artificial muscles with controllable geometries and excellent performance in the future.