This article presents the extraction and effect of alkali treatment on the physical, chemical, tensile, and thermal characteristics of fiber strands obtained from Napier grass, a renewable biomass. In order to improve these properties, the Napier grass fiber strands were treated with sodium hydroxide. The alkali treatment was carried out using NaOH solution at three different concentrations (5, 10, and 15%) for 2 h. Characterization of untreated and alkali-treated Napier grass fiber strands was carried out by studying the chemical composition, surface morphology, functional group variation, crystallinity, and tensile and thermal behavior. It was found that untreated fiber strands have lower cellulose content, crystallinity, tensile properties, and thermal stability than alkali-treated fiber strands. Napier grass fiber strands treated with 10% NaOH showed optimum tensile strength, modulus, and percentage elongation with an improvement of 51.9, 47.3, and 12.1% respectively. Based on the properties determined for alkali-treated Napier grass fiber strands, we expect that these fibers will be suitable for use as a reinforcement in natural fiber composites.

To obtain cellulose microfibers from Palmyra palm fruit fibers, a new succession of specific chemical treatments including acidified chlorination, alkalization, and acid hydrolysis have been developed. Cellulose microfibers obtained were characterized by different techniques. The chemical analysis indicated an increase in α-cellulose content and decrease in lignin and hemicellulose for the cellulose microfibers over raw fibers. Fourier transform infrared and ¹³C NMR spectra confirmed the removal of non-cellulosic (lignin and hemicellulose) components after chemical treatments. The X-ray diffraction results revealed that the cellulose I was partly transformed into cellulose II by chemical treatments and the crystallinity index of cellulose microfibers was significantly increased as compared to raw fibers owing to removal of non-cellulosic components. Thermogravimetric analysis results demonstrated that the thermal stability was enhanced noticeably for cellulose microfibers than for the raw fibers. The scanning electron micrographs illustrated cleaner and rough surfaces for the cellulose microfibers when compared to those of raw fibers.

Napier grass fiber strands were used as reinforcement to obtain composites with epoxy resin as matrix. To improve the surface, these fiber strands were treated with alkali solution. The composites were prepared by means of hand lay-up molding, then the effects of Napier grass fiber strand loading on mechanical properties such as tensile, flexural and impact, interfacial bonding, and chemical resistance were investigated. The composite with 20 wt.% Napier grass fiber strands gives excellent mechanical properties and chemical resistance, showing that it has the best bonding and adhesion of the composites. SEM micrographs of fractured and worn surfaces clearly demonstrate the interfacial adhesion between fiber and matrix. Alkali-treated Napier grass fiber strand–reinforced composites have better resistance to water and chemicals than the untreated fiber strand composites.