Oxide-supported Ag nanoparticles have been widely reported as a good approach to improve the stability and reduce the cost of photocatalysts. In this work, a Ag-nanoparticles-doped porous ZnO photocatalyst was prepared by using metal–organic frameworks as a sacrificial precursor and the catalytic activity over 4-nitrophenol was determined. The Ag-nanoparticles-doped porous ZnO heterostructure was evaluated by UV, XRD, and FETEM, and the catalytic rate constant was calculated by the change in absorbance value at 400 nm of 4-nitrophenol. The photocatalyst with a heterogeneous structure is visible, light-responsive, and beneficial to accelerating the catalytic rate. Under visible light irradiation, the heterostructure showed excellent catalytic activity over 4-nitrophenol due to the hot electrons induced by the localized surface plasmon resonance of Ag nanoparticles. Additionally, the catalytic rates of 4 nm/30 nm Ag nanoparticles and porous/nonporous ZnO were compared. We found that the as-prepared Ag-nanoparticles-doped porous ZnO heterostructure catalyst showed enhanced catalytic performance due to the synergetic effect of Ag nanoparticles and porous ZnO. This study provides a novel heterostructure photocatalyst with potential applications in solar energy and pollutant disposal.

The plasmonic photothermal effects of metal nanostructures have recently become a new priority of studies in the field of nano-optics. Controllable plasmonic nanostructures with a wide range of responses are crucial for effective photothermal effects and their applications. In this work, self-assembled aluminum nano-islands (Al NIs) with a thin alumina layer are designed as a plasmonic photothermal structure to achieve nanocrystal transformation via multi-wavelength excitation. The plasmonic photothermal effects can be controlled by the thickness of the Al₂O₃ and the intensity and wavelength of the laser illumination. In addition, Al NIs with an alumina layer have good photothermal conversion efficiency even in low temperature environments, and the efficiency will not decline significantly after storage in air for 3 months. Such an inexpensive Al/Al₂O₃ structure with a multi-wavelength response provides an efficient platform for rapid nanocrystal transformation and a potential application for the wide-band absorption of solar energy.