The aim of this study was to investigate the effect of recycling on polypropylene (PP) and wood-fiber thermoplastic composites (WPCs) using a co-rotating twin-screw extruder. After nine extrusion passes microscopy studies confirmed that the fiber length decreased with the increased number of recycling passes but the increased processing time also resulted in excellent dispersion and interfacial adhesion of the wood fibers in the PP matrix. Thermal, rheological, and mechanical properties were studied. The repeated extrusion passes had minimal effect on thermal behavior and the viscosity decreased with an increased number of passes, indicating slight degradation. The recycling processes had an effect on the tensile strength of WPCs while the effect was minor on the PP. However, even after the nine recycling passes the strength of WPC was considerably better (37 MPa) compared to PP (28 MPa). The good degree of property retention after recycling makes this recycling strategy a viable alternative to discarding the materials. Thus, it has been demonstrated that, by following the most commonly used extrusion process, WPCs can be recycled several times and this methodology can be industrially adapted for the manufacturing of recycled products.

Underutilized co‐ and by‐products are upgraded into materials with functional properties. The utilization of mushroom farming residues is investigated, specifically mushroom residues and spent mushroom substrate – whose chemical composition is determined – to produce cosmetic face masks, packaging films, and oil sorbents. Flexible mushroom sheets exhibit conformability and antioxidant activity between 82 and 94%, and better tensile strength in comparison with commercial cosmetic masks, making them suitable for such applications. Plasticization with glycerol increases the flexibility and tensile strain from ≈1 to 45% and moisture sorption from 32 to 100 wt.%. Spent mushroom substrate pulp yields stiff and strong rigid sheets with Young's moduli of 5 GPa and tensile strengths of 42 MPa. These sheets show 100% antioxidant activity, having hydrophobic behavior and oxygen barrier properties in dry conditions, and thus are promising for bioactive packaging applications. Foamed spent mushroom substrate sorbents demonstrate high affinity for both oil and water, with a water and oil uptake of 21 and 28 times their weight, respectively, while maintaining structural integrity. These properties make the foams viable as bio‐based oil sorbents, highlighting the potential of by‐products for advanced functional materials.

In this study, the possibility of adding nanocellulose and its dispersion to polyamide 6 (PA6), a polymer with a high melting temperature, is investigated using melt extrusion. The main challenges of the extrusion of these materials are achieving a homogeneous dispersion and avoiding the thermal degradation of nanocellulose. These challenges are overcome by using an aqueous suspension of never-dried nanocellulose, which is pumped into the molten polymer without any chemical modification or drying. Furthermore, polyethylene glycol is tested as a dispersant for nanocellulose. The dispersion, thermal degradation, and mechanical and viscoelastic properties of the nanocomposites are studied. The results show that the dispersant has a positive impact on the dispersion of nanocellulose and that the liquid-assisted melt compounding does not cause the degradation of nanocellulose. The addition of only 0.5 wt.% nanocellulose increases the stiffness of the neat polyamide 6 from 2 to 2.3 GPa and shifts the tan δ peak toward higher temperatures, indicating an interaction between PA6 and nanocellulose. The addition of the dispersant decreases the strength and modulus but has a significant effect on the elongation and toughness. To further enhance the mechanical properties of the nanocomposites, solid-state drawing is used to create an oriented structure in the polymer and nanocomposites. The orientation greatly improves its mechanical properties, and the oriented nanocomposite with polyethylene glycol as dispersant exhibits the best alignment and properties: with orientation, the strength increases from 52 to 221 MPa, modulus from 1.4 to 2.8 GPa, and toughness 30 to 33 MJ m⁻³ in a draw ratio of 2.5. This study shows that nanocellulose can be added to PA6 by liquid-assisted extrusion with good dispersion and without degradation and that the orientation of the structure is a highly-effective method for producing thermoplastic nanocomposites with excellent mechanical properties.

Wood–polymer composites (WPCs) with polypropylene (PP) matrix suffer from low toughness, and fossil-based impact modifiers are used to improve their performance. Material substitution of virgin fossil-based materials and material recycling are key aspects of sustainable development and therefore recycled denim fabric, and elastomer were evaluated to replace the virgin elastomer modifier commonly used in commercial WPCs. Microtomography images showed that the extrusion process fibrillated the denim fabric into long, thin fibers that were well dispersed within the WPC, while the recycled elastomer was found close to the wood fibers, acting as a soft interphase between the wood fibers and PP. The fracture toughness (K_IC) of the WPC with recycled denim fabric matched the commercial WPC which was 1.4 MPa m^1/2 and improved the composite tensile strength by 18% and E-modulus by 54%. Recycled elastomer resulted in slightly lower K_IC, 1.1 MPa m^1/2, as well as strength and modulus while increasing elongation and contributing to toughness. The results of this study showed that recycled materials can potentially be used to replace virgin fossil-based elastomeric modifiers in commercial WPCs, thereby reducing the CO₂ footprint by 23% and contributing to more efficient use of resources.